Surface modified ZnS nanoparticles were prepared in this work. Infrared spectroscopy (IR), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS) were used to investigate the structure, size, and morphology of the modified ZnS nanoparticles. It was found that the average diameter of the coated ZnS nanoparticles was about 4 nm, and the dispersion capacity and oxidative stability could be improved effectively by surface modification with DDP.

源语言	英语
页（从-至）	474
页数	1
期刊	Gaodeng Xuexiao Huaxue Xuebao/Chemical Journal of Chinese Universities
卷	21
期	3
出版状态	已出版 - 10 3月 2000
已对外发布	是

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{1c1558a3ac234255818253ea77e02532,

title = "Preparation of Oil-soluble ZnS Nanoparticles",

abstract = "Surface modified ZnS nanoparticles were prepared in this work. Infrared spectroscopy (IR), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS) were used to investigate the structure, size, and morphology of the modified ZnS nanoparticles. It was found that the average diameter of the coated ZnS nanoparticles was about 4 nm, and the dispersion capacity and oxidative stability could be improved effectively by surface modification with DDP.",

keywords = "Dispersion, Nanoparticles, Surface modification, ZnS",

author = "Shuang Chen and Liu, {Wei Min}",

year = "2000",

month = mar,

day = "10",

language = "英语",

volume = "21",

pages = "474",

journal = "Gaodeng Xuexiao Huaxue Xuebao/Chemical Journal of Chinese Universities",

issn = "0251-0790",

publisher = "Higher Education Press Limited Company",

number = "3",

}

TY - JOUR

T1 - Preparation of Oil-soluble ZnS Nanoparticles

AU - Chen, Shuang

AU - Liu, Wei Min

PY - 2000/3/10

Y1 - 2000/3/10

N2 - Surface modified ZnS nanoparticles were prepared in this work. Infrared spectroscopy (IR), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS) were used to investigate the structure, size, and morphology of the modified ZnS nanoparticles. It was found that the average diameter of the coated ZnS nanoparticles was about 4 nm, and the dispersion capacity and oxidative stability could be improved effectively by surface modification with DDP.

AB - Surface modified ZnS nanoparticles were prepared in this work. Infrared spectroscopy (IR), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS) were used to investigate the structure, size, and morphology of the modified ZnS nanoparticles. It was found that the average diameter of the coated ZnS nanoparticles was about 4 nm, and the dispersion capacity and oxidative stability could be improved effectively by surface modification with DDP.

KW - Dispersion

KW - Nanoparticles

KW - Surface modification

KW - ZnS

UR - http://www.scopus.com/inward/record.url?scp=0347647505&partnerID=8YFLogxK

M3 - 文章

AN - SCOPUS:0347647505

SN - 0251-0790

VL - 21

SP - 474

JO - Gaodeng Xuexiao Huaxue Xuebao/Chemical Journal of Chinese Universities

JF - Gaodeng Xuexiao Huaxue Xuebao/Chemical Journal of Chinese Universities

IS - 3

ER -

Preparation of Oil-soluble ZnS Nanoparticles

摘要

其它文件与链接

指纹

引用此