Oxidation behavior of 2D C/SiC composites coated with multi-layer SiC/Si-B-C/SiC coatings under wet oxygen atmosphere

Yongsheng Liu; Jiajia Wan; Xinzhang Zuo; Laifei Cheng; Litong Zhang

doi:10.1016/j.apsusc.2015.06.153

Oxidation behavior of 2D C/SiC composites coated with multi-layer SiC/Si-B-C/SiC coatings under wet oxygen atmosphere

Yongsheng Liu, Jiajia Wan, Xinzhang Zuo, Laifei Cheng, Litong Zhang

材料学院

Northwestern Polytechnical University Xian

科研成果: 期刊稿件 › 文章 › 同行评审

48 引用（Scopus）

摘要

Oxidation behavior of 2D C/SiC composites coated with multi-layer SiC/Si-B-C/SiC coatings had been investigated under wet oxygen atmosphere for 50 h. The multi-layer SiC/Si-B-C/SiC coatings showed excellent oxidation protection at all temperatures due to the effective crack sealing of borosilicate glass. Especially, the coated samples also had a high residual strength retention ratio (106.7%) and a low weight loss (0.058%) after oxidation at 1000 °C for 50 h. However, the increasing water partial pressure could improve the volatilization of borosilicate glass and weaken the sealing function of the glass at some extent when the oxidation temperature was above 1200 °C.

源语言	英语
页（从-至）	214-223
页数	10
期刊	Applied Surface Science
卷	353
DOI	https://doi.org/10.1016/j.apsusc.2015.06.153
出版状态	已出版 - 30 10月 2015

访问文件

10.1016/j.apsusc.2015.06.153

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{27d10c4cdfe9484abebfc081c87253ba,

title = "Oxidation behavior of 2D C/SiC composites coated with multi-layer SiC/Si-B-C/SiC coatings under wet oxygen atmosphere",

abstract = "Oxidation behavior of 2D C/SiC composites coated with multi-layer SiC/Si-B-C/SiC coatings had been investigated under wet oxygen atmosphere for 50 h. The multi-layer SiC/Si-B-C/SiC coatings showed excellent oxidation protection at all temperatures due to the effective crack sealing of borosilicate glass. Especially, the coated samples also had a high residual strength retention ratio (106.7%) and a low weight loss (0.058%) after oxidation at 1000 °C for 50 h. However, the increasing water partial pressure could improve the volatilization of borosilicate glass and weaken the sealing function of the glass at some extent when the oxidation temperature was above 1200 °C.",

keywords = "2D C/SiC composites, Multi-layer SiC/Si-B-C/SiC coatings, Oxidation behavior, Wet oxygen atmosphere",

author = "Yongsheng Liu and Jiajia Wan and Xinzhang Zuo and Laifei Cheng and Litong Zhang",

year = "2015",

month = oct,

day = "30",

doi = "10.1016/j.apsusc.2015.06.153",

language = "英语",

volume = "353",

pages = "214--223",

journal = "Applied Surface Science",

issn = "0169-4332",

publisher = "Elsevier B.V.",

}

TY - JOUR

T1 - Oxidation behavior of 2D C/SiC composites coated with multi-layer SiC/Si-B-C/SiC coatings under wet oxygen atmosphere

AU - Liu, Yongsheng

AU - Wan, Jiajia

AU - Zuo, Xinzhang

AU - Cheng, Laifei

AU - Zhang, Litong

PY - 2015/10/30

Y1 - 2015/10/30

N2 - Oxidation behavior of 2D C/SiC composites coated with multi-layer SiC/Si-B-C/SiC coatings had been investigated under wet oxygen atmosphere for 50 h. The multi-layer SiC/Si-B-C/SiC coatings showed excellent oxidation protection at all temperatures due to the effective crack sealing of borosilicate glass. Especially, the coated samples also had a high residual strength retention ratio (106.7%) and a low weight loss (0.058%) after oxidation at 1000 °C for 50 h. However, the increasing water partial pressure could improve the volatilization of borosilicate glass and weaken the sealing function of the glass at some extent when the oxidation temperature was above 1200 °C.

AB - Oxidation behavior of 2D C/SiC composites coated with multi-layer SiC/Si-B-C/SiC coatings had been investigated under wet oxygen atmosphere for 50 h. The multi-layer SiC/Si-B-C/SiC coatings showed excellent oxidation protection at all temperatures due to the effective crack sealing of borosilicate glass. Especially, the coated samples also had a high residual strength retention ratio (106.7%) and a low weight loss (0.058%) after oxidation at 1000 °C for 50 h. However, the increasing water partial pressure could improve the volatilization of borosilicate glass and weaken the sealing function of the glass at some extent when the oxidation temperature was above 1200 °C.

KW - 2D C/SiC composites

KW - Multi-layer SiC/Si-B-C/SiC coatings

KW - Oxidation behavior

KW - Wet oxygen atmosphere

UR - http://www.scopus.com/inward/record.url?scp=84941958442&partnerID=8YFLogxK

U2 - 10.1016/j.apsusc.2015.06.153

DO - 10.1016/j.apsusc.2015.06.153

M3 - 文章

AN - SCOPUS:84941958442

SN - 0169-4332

VL - 353

SP - 214

EP - 223

JO - Applied Surface Science

JF - Applied Surface Science

ER -

Oxidation behavior of 2D C/SiC composites coated with multi-layer SiC/Si-B-C/SiC coatings under wet oxygen atmosphere

摘要

访问文件

其它文件与链接

指纹

引用此