7475-T761航空铝合金的物相分析

Mao Hua Li; Yan Qing Yang; Chang Ping Tang; Zhi Long Chen; Jia Xuan Mo

doi:10.13289/j.issn.1009-6264.2021-0137

7475-T761航空铝合金的物相分析

Mao Hua Li, Yan Qing Yang, Chang Ping Tang, Zhi Long Chen, Jia Xuan Mo

材料学院

Hunan University of Science and Technology

科研成果: 期刊稿件 › 文章 › 同行评审

摘要

Microstructure of 7475-T761 aviation aluminum alloy was studied by means of transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDX), selective area electron diffraction (SAED), micro beam diffraction (μ-D), high resolution transmission electron microscopy (HRTEM) and high angle annular dark field scanning transmission electron microscopy (HAADF-STEM). The results show that the microstructure of the 7475-T761 aluminum alloy is mainly composed of dispersed phase, aging strengthening phase and impurity phase. The dispersed phase is E phase (Al₁₈Cr₂Mg₃) with various morphology, and the η phase is easy to precipitate inhomogeneously at the E/Al interface. The aging strengthening phases are mainly composed of GPⅡ zones, η' phase and η phase. The impurity phases are mainly composed of Al₇Cu₂Fe, FeAl₃ and Si-rich phases.

投稿的翻译标题	Phase analysis of 7475-T761 aviation aluminum alloy
源语言	繁体中文
页（从-至）	68-75
页数	8
期刊	Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment
卷	42
期	9
DOI	https://doi.org/10.13289/j.issn.1009-6264.2021-0137
出版状态	已出版 - 25 9月 2021

关键词

7475 aluminum alloy
Aging strengthening phase
Dispersed phase
Impurity phase

访问文件

10.13289/j.issn.1009-6264.2021-0137

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{f8ff721e67b1427e8ca29212d7443140,

title = "7475-T761航空铝合金的物相分析",

abstract = "Microstructure of 7475-T761 aviation aluminum alloy was studied by means of transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDX), selective area electron diffraction (SAED), micro beam diffraction (μ-D), high resolution transmission electron microscopy (HRTEM) and high angle annular dark field scanning transmission electron microscopy (HAADF-STEM). The results show that the microstructure of the 7475-T761 aluminum alloy is mainly composed of dispersed phase, aging strengthening phase and impurity phase. The dispersed phase is E phase (Al18Cr2Mg3) with various morphology, and the η phase is easy to precipitate inhomogeneously at the E/Al interface. The aging strengthening phases are mainly composed of GPⅡ zones, η' phase and η phase. The impurity phases are mainly composed of Al7Cu2Fe, FeAl3 and Si-rich phases.",

keywords = "7475 aluminum alloy, Aging strengthening phase, Dispersed phase, Impurity phase",

author = "Li, {Mao Hua} and Yang, {Yan Qing} and Tang, {Chang Ping} and Chen, {Zhi Long} and Mo, {Jia Xuan}",

year = "2021",

month = sep,

day = "25",

doi = "10.13289/j.issn.1009-6264.2021-0137",

language = "繁体中文",

volume = "42",

pages = "68--75",

journal = "Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment",

issn = "1009-6264",

publisher = "Chinese Mechanical Engineering Society",

number = "9",

}

TY - JOUR

T1 - 7475-T761航空铝合金的物相分析

AU - Li, Mao Hua

AU - Yang, Yan Qing

AU - Tang, Chang Ping

AU - Chen, Zhi Long

AU - Mo, Jia Xuan

PY - 2021/9/25

Y1 - 2021/9/25

N2 - Microstructure of 7475-T761 aviation aluminum alloy was studied by means of transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDX), selective area electron diffraction (SAED), micro beam diffraction (μ-D), high resolution transmission electron microscopy (HRTEM) and high angle annular dark field scanning transmission electron microscopy (HAADF-STEM). The results show that the microstructure of the 7475-T761 aluminum alloy is mainly composed of dispersed phase, aging strengthening phase and impurity phase. The dispersed phase is E phase (Al18Cr2Mg3) with various morphology, and the η phase is easy to precipitate inhomogeneously at the E/Al interface. The aging strengthening phases are mainly composed of GPⅡ zones, η' phase and η phase. The impurity phases are mainly composed of Al7Cu2Fe, FeAl3 and Si-rich phases.

AB - Microstructure of 7475-T761 aviation aluminum alloy was studied by means of transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDX), selective area electron diffraction (SAED), micro beam diffraction (μ-D), high resolution transmission electron microscopy (HRTEM) and high angle annular dark field scanning transmission electron microscopy (HAADF-STEM). The results show that the microstructure of the 7475-T761 aluminum alloy is mainly composed of dispersed phase, aging strengthening phase and impurity phase. The dispersed phase is E phase (Al18Cr2Mg3) with various morphology, and the η phase is easy to precipitate inhomogeneously at the E/Al interface. The aging strengthening phases are mainly composed of GPⅡ zones, η' phase and η phase. The impurity phases are mainly composed of Al7Cu2Fe, FeAl3 and Si-rich phases.

KW - 7475 aluminum alloy

KW - Aging strengthening phase

KW - Dispersed phase

KW - Impurity phase

UR - http://www.scopus.com/inward/record.url?scp=85118473038&partnerID=8YFLogxK

U2 - 10.13289/j.issn.1009-6264.2021-0137

DO - 10.13289/j.issn.1009-6264.2021-0137

M3 - 文章

AN - SCOPUS:85118473038

SN - 1009-6264

VL - 42

SP - 68

EP - 75

JO - Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment

JF - Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment

IS - 9

ER -

7475-T761航空铝合金的物相分析

摘要

关键词

访问文件

其它文件与链接

指纹

引用此