The oxidation behaviors of indefinite chill roll and high speed steel materials

Indefinite chill (IC) roll and high speed steel (HSS) materials have been widely employed to manufacture work rolls as latter and former stands in hot rolling mills. The oxidation of work rolls is of importance for the surface quality of the rolled workpieces. The isothermal oxidation of the IC and HSS materials was conducted at 650^◦C and 700^◦C in both dry air and humid air. The isothermal oxidation curves indicate that HSS shows faster kinetics than the IC materials in dry air, whereas the opposite occurred in humid air. The oxide scales of the IC materials after the oxidation in both dry air and humid air are made up of two oxide phases. Two oxide phases were found when the HSS oxidized in the dry air and three oxide phases were found when oxidized in the humid air.