title = "The effects of BaF2 addition on melt-processed YBa2Cu 3O7-x superconductors",
abstract = "The effects of BaF2 on thermal behavior and microstructure of melt-processed YBCO superconductors have been investigated. The differential thermal analysis (DTA) results indicated that the peritectic decomposition temperature of YBCO precursor powder was lowered when BaF2 was added (from 1020°C to 976°C). The peritectic decomposition temperature was lowest at the content of 5 wt.% BaF2, and the variation of melting temperature was not significant above 5 wt.% BaF2 The microstructures of the doped samples have been observed by scanning electron microscopy (SEM). The results showed that the appropriate addition of BaF2 had no negative effect on the microstructure of YBCO.",
keywords = "BaF addition, Melt-processed, Thermal behavior, YBCO",
author = "Feng Jianqing and Zhou Lian and Lu Yafeng and Zhang Pingxiang and Xu Xiaoyan and Chen Shaokai and Zhang Cuiping",
year = "2007",
doi = "10.4028/www.scientific.net/MSF.546-549.2075",
language = "英语",
isbn = "0878494324",
series = "Materials Science Forum",
publisher = "Trans Tech Publications Ltd",
number = "PART 4",
pages = "2075--2078",
booktitle = "Progress in Light Metals, Aerospace Materials and Superconductors",
edition = "PART 4",
note = "2006 Beijing International Materials Week, 2006 BIMW - International Conference on Superconducting Materials, ICSM 2006 ; Conference date: 25-06-2006 Through 30-06-2006",
}