Tensile fracture behavior and strength distribution of SiCf/SiC composites with different SiBN interface thicknesses

Yongsheng Liu, Nan Chai, Hailong Qin, Zan Li, Fang Ye, Laifei Cheng

科研成果: 期刊稿件文章同行评审

25 引用 (Scopus)

摘要

The borosilicate nitride (SiBN) interface was firstly fabricated in SiC fibers reinforced SiC matrix (SiCf/SiC) composites by low-pressure chemical vapor infiltration (LPCVI). Tensile fracture behavior and strength distribution of SiCf/SiC composites with different SiBN thicknesses were investigated. The results showed that the tensile strength first increased and then declined with increasing interface thickness. The maximum value of tensile strength was 550.8 MPa with a 1000 nm SiBN interface. Non-brittle tensile fracture behavior of SiCf/SiC composites with a SiBN interface was demonstrated. The pull-out length and amount of fibers had a similar variation trend with increasing interface thickness. Strength distributions of SiCf/SiC composites with different interface thicknesses followed Weibull distribution with two parameters. Weibull modules of tensile strength increased first, and then decreased with increasing interface thickness. The maximum value of the Weibull module was 11.0224 when the interface thickness was 1000 nm, which indicated the highest reliability of SiCf/SiC composites. The mean value of tensile strength for SiCf/SiC composite with 1000 nm interface was 576.82 MPa obtained by the theory calculation, which was consistent with the result of experiment (550.8 MPa) very well.

源语言英语
页(从-至)1609-1616
页数8
期刊Ceramics International
41
1
DOI
出版状态已出版 - 2015

指纹

探究 'Tensile fracture behavior and strength distribution of SiCf/SiC composites with different SiBN interface thicknesses' 的科研主题。它们共同构成独一无二的指纹。

引用此