Strengthening of a high strength Fe85Ni15 alloy by tempering treatment

Yonghai Kang; Licai Fu; Jiqiang Ma; Fei Li; Zhuhui Qiao; Jun Yang; Qinling Bi; Weimin Liu

doi:10.1016/j.msea.2013.04.028

Strengthening of a high strength Fe₈₅Ni₁₅ alloy by tempering treatment

Yonghai Kang, Licai Fu, Jiqiang Ma, Fei Li, Zhuhui Qiao, Jun Yang, Qinling Bi, Weimin Liu

科研成果: 期刊稿件 › 文章 › 同行评审

4 引用（Scopus）

摘要

A high-strength Fe₈₅Ni₁₅ alloy with lath martensitic structure was obtained by the self-propagating high-temperature synthesis technique. After tempering at 500 °C for 2 h, the hardness increased from 3.8 to 5.1 GPa, and the compression yield strength increased from about 1100 to 1500 MPa without much sacrifice of ductility. The strengthening effect might be attributed to the evolution of lath martensitic morphology and the reverse martensitic transformation.

源语言	英语
页（从-至）	316-319
页数	4
期刊	Materials Science and Engineering: A
卷	576
DOI	https://doi.org/10.1016/j.msea.2013.04.028
出版状态	已出版 - 1 8月 2013
已对外发布	是

访问文件

10.1016/j.msea.2013.04.028

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{1d518849a4a049c3bd2fba4f89696bd2,

title = "Strengthening of a high strength Fe85Ni15 alloy by tempering treatment",

abstract = "A high-strength Fe85Ni15 alloy with lath martensitic structure was obtained by the self-propagating high-temperature synthesis technique. After tempering at 500 °C for 2 h, the hardness increased from 3.8 to 5.1 GPa, and the compression yield strength increased from about 1100 to 1500 MPa without much sacrifice of ductility. The strengthening effect might be attributed to the evolution of lath martensitic morphology and the reverse martensitic transformation.",

keywords = "Aging, Ferrous alloys, Martensite, Nanostructured materials, Recrystallization",

author = "Yonghai Kang and Licai Fu and Jiqiang Ma and Fei Li and Zhuhui Qiao and Jun Yang and Qinling Bi and Weimin Liu",

note = "Publisher Copyright: {\textcopyright} 2013 Elsevier B.V.",

year = "2013",

month = aug,

day = "1",

doi = "10.1016/j.msea.2013.04.028",

language = "英语",

volume = "576",

pages = "316--319",

journal = "Materials Science and Engineering: A",

issn = "0921-5093",

publisher = "Elsevier Ltd",

}

TY - JOUR

T1 - Strengthening of a high strength Fe85Ni15 alloy by tempering treatment

AU - Kang, Yonghai

AU - Fu, Licai

AU - Ma, Jiqiang

AU - Li, Fei

AU - Qiao, Zhuhui

AU - Yang, Jun

AU - Bi, Qinling

AU - Liu, Weimin

PY - 2013/8/1

Y1 - 2013/8/1

N2 - A high-strength Fe85Ni15 alloy with lath martensitic structure was obtained by the self-propagating high-temperature synthesis technique. After tempering at 500 °C for 2 h, the hardness increased from 3.8 to 5.1 GPa, and the compression yield strength increased from about 1100 to 1500 MPa without much sacrifice of ductility. The strengthening effect might be attributed to the evolution of lath martensitic morphology and the reverse martensitic transformation.

AB - A high-strength Fe85Ni15 alloy with lath martensitic structure was obtained by the self-propagating high-temperature synthesis technique. After tempering at 500 °C for 2 h, the hardness increased from 3.8 to 5.1 GPa, and the compression yield strength increased from about 1100 to 1500 MPa without much sacrifice of ductility. The strengthening effect might be attributed to the evolution of lath martensitic morphology and the reverse martensitic transformation.

KW - Aging

KW - Ferrous alloys

KW - Martensite

KW - Nanostructured materials

KW - Recrystallization

UR - http://www.scopus.com/inward/record.url?scp=84877086804&partnerID=8YFLogxK

U2 - 10.1016/j.msea.2013.04.028

DO - 10.1016/j.msea.2013.04.028

M3 - 文章

AN - SCOPUS:84877086804

SN - 0921-5093

VL - 576

SP - 316

EP - 319

JO - Materials Science and Engineering: A

JF - Materials Science and Engineering: A

ER -

Strengthening of a high strength Fe85Ni15 alloy by tempering treatment

摘要

访问文件

其它文件与链接

指纹

引用此

Strengthening of a high strength Fe₈₅Ni₁₅ alloy by tempering treatment