Research on microstructure and oxidation resistance of SiC/Al-Si coating for carbon-carbon composites

Min Huang; Ke Zhi Li; He Jun Li; Qian Gang Fu; Guo Dong Sun

Research on microstructure and oxidation resistance of SiC/Al-Si coating for carbon-carbon composites

Min Huang, Ke Zhi Li, He Jun Li, Qian Gang Fu, Guo Dong Sun

材料学院

Northwestern Polytechnical University Xian

科研成果: 期刊稿件 › 文章 › 同行评审

2 引用（Scopus）

摘要

Al-Si alloy coating was prepared on the surface of SiC coated carbon-carbon composites by slurry method. Microstructure and oxidation resistance of as-prepared SiC/Al-Si multi-layer coating were studied by XRD, SEM, and isothermal oxidation test under 1500°C in air respectively. The results showed that Al_3.21Si_0.47 and a few Al₂O₃ were the main phase of Al-Si outer coating. The thickness of SiC/Al-Si multi-layer coating was about 120 μm and without penetrable cracks. The oxidation resistance of SiC/Al-Si multi-layer coating was obviously better than that of single SiC coating. The mass loss of SiC/Al-Si multi-layer coated carbon-carbon composites was less than 5% (mass fraction) after oxidation for 17h.

源语言	英语
页（从-至）	43-46
页数	4
期刊	Cailiao Gongcheng/Journal of Materials Engineering
期	4
出版状态	已出版 - 4月 2007

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{faa7b4ae13574c6684d9f371ed1bb322,

title = "Research on microstructure and oxidation resistance of SiC/Al-Si coating for carbon-carbon composites",

abstract = "Al-Si alloy coating was prepared on the surface of SiC coated carbon-carbon composites by slurry method. Microstructure and oxidation resistance of as-prepared SiC/Al-Si multi-layer coating were studied by XRD, SEM, and isothermal oxidation test under 1500°C in air respectively. The results showed that Al3.21Si0.47 and a few Al2O3 were the main phase of Al-Si outer coating. The thickness of SiC/Al-Si multi-layer coating was about 120 μm and without penetrable cracks. The oxidation resistance of SiC/Al-Si multi-layer coating was obviously better than that of single SiC coating. The mass loss of SiC/Al-Si multi-layer coated carbon-carbon composites was less than 5% (mass fraction) after oxidation for 17h.",

keywords = "Al-Si alloy, C/C composite, Coating, Oxidation resistance, SiC",

author = "Min Huang and Li, {Ke Zhi} and Li, {He Jun} and Fu, {Qian Gang} and Sun, {Guo Dong}",

year = "2007",

month = apr,

language = "英语",

pages = "43--46",

journal = "Cailiao Gongcheng/Journal of Materials Engineering",

issn = "1001-4381",

publisher = "Science Press ",

number = "4",

}

TY - JOUR

T1 - Research on microstructure and oxidation resistance of SiC/Al-Si coating for carbon-carbon composites

AU - Huang, Min

AU - Li, Ke Zhi

AU - Li, He Jun

AU - Fu, Qian Gang

AU - Sun, Guo Dong

PY - 2007/4

Y1 - 2007/4

N2 - Al-Si alloy coating was prepared on the surface of SiC coated carbon-carbon composites by slurry method. Microstructure and oxidation resistance of as-prepared SiC/Al-Si multi-layer coating were studied by XRD, SEM, and isothermal oxidation test under 1500°C in air respectively. The results showed that Al3.21Si0.47 and a few Al2O3 were the main phase of Al-Si outer coating. The thickness of SiC/Al-Si multi-layer coating was about 120 μm and without penetrable cracks. The oxidation resistance of SiC/Al-Si multi-layer coating was obviously better than that of single SiC coating. The mass loss of SiC/Al-Si multi-layer coated carbon-carbon composites was less than 5% (mass fraction) after oxidation for 17h.

AB - Al-Si alloy coating was prepared on the surface of SiC coated carbon-carbon composites by slurry method. Microstructure and oxidation resistance of as-prepared SiC/Al-Si multi-layer coating were studied by XRD, SEM, and isothermal oxidation test under 1500°C in air respectively. The results showed that Al3.21Si0.47 and a few Al2O3 were the main phase of Al-Si outer coating. The thickness of SiC/Al-Si multi-layer coating was about 120 μm and without penetrable cracks. The oxidation resistance of SiC/Al-Si multi-layer coating was obviously better than that of single SiC coating. The mass loss of SiC/Al-Si multi-layer coated carbon-carbon composites was less than 5% (mass fraction) after oxidation for 17h.

KW - Al-Si alloy

KW - C/C composite

KW - Coating

KW - Oxidation resistance

KW - SiC

UR - http://www.scopus.com/inward/record.url?scp=34248347493&partnerID=8YFLogxK

M3 - 文章

AN - SCOPUS:34248347493

SN - 1001-4381

SP - 43

EP - 46

JO - Cailiao Gongcheng/Journal of Materials Engineering

JF - Cailiao Gongcheng/Journal of Materials Engineering

IS - 4

ER -

Research on microstructure and oxidation resistance of SiC/Al-Si coating for carbon-carbon composites

摘要

其它文件与链接

指纹

引用此