Multimodal γ′ phase precipitation and mechanical properties of Co-based superalloys with Ta addition

Jiachen Zhang, Qingze Na, Tiantian Ma, Fan Lu, Rui Li, Juan Wang, Caixia Wang, Guojun Zhang, Haijun Su, Lin Liu

科研成果: 期刊稿件文章同行评审

摘要

Combined with transmission electron microscopy (TEM), atom probe tomography (APT) and density functional theory (DFT) calculations, the effects of tantalum (Ta) on the microstructural features of Co-based superalloys were investigated, focusing on how multimodal γ′ phases influence the alloy's yield strength. The findings indicate that Ta strongly partitions into the primary γ′ phase and occupied the B-sites of A3B-L12 structure, significantly increasing its solvus temperature, volume fraction, and antiphase boundary (APB) energy, thereby enhancing high-temperature mechanical properties. The addition of 2 at.% Ta notably inhibits secondary γ′ precipitation due to a decrease in nucleation drive caused by the reduced Gibbs free energy change. The diffuse distribution of secondary γ′ phases provide more dislocation pinning sites within the alloy, resulting in mechanical properties that are less sensitive to temperature variations. This is evidenced by a gentler decline in yield strength with increasing temperature.

源语言英语
文章编号148250
期刊Materials Science and Engineering: A
932
DOI
出版状态已出版 - 6月 2025

指纹

探究 'Multimodal γ′ phase precipitation and mechanical properties of Co-based superalloys with Ta addition' 的科研主题。它们共同构成独一无二的指纹。

引用此