Microstructure and properties of NbTi superconducting composite wire for ITER

Jianfeng Li; Pingxiang Zhang; Xianghong Liu; Jinshan Li; Yong Feng; Tiancheng Wang; Shejun Du; Weitao Liu; G. Grunblatt; C. Verwaerde; G. K. Hoang

Microstructure and properties of NbTi superconducting composite wire for ITER

Jianfeng Li, Pingxiang Zhang, Xianghong Liu, Jinshan Li, Yong Feng, Tiancheng Wang, Shejun Du, Weitao Liu, G. Grunblatt, C. Verwaerde, G. K. Hoang

材料学院

科研成果: 期刊稿件 › 文章 › 同行评审

10 引用（Scopus）

摘要

This paper shows the results of R&D program carried out to optimize NbTi wires for the Poloidal Field (PF) coils of ITER. The influence of heat treatment on the microstructure was investigated by using TEM to find the relations between the microstructure and the critical current densities at 4.2 K for NbTi superconducting composite wire. Typical microstructure (in transverse cross-section) shows α-Ti pinning centers dispersed within the superconducting β-NbTi matrix with strong fold and curl for the NbTi wire with high critical current density at 4.2 K. It is believed that the higher temperature is beneficial to a higher Jc value at 4.2 K, but the Jc values slightly decrease with increasing the heat treatment times.

源语言	英语
页（从-至）	263-265
页数	3
期刊	Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering
卷	38
期	2
出版状态	已出版 - 2月 2009

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{af335769bb32476caee0e7be2e4bbd75,

title = "Microstructure and properties of NbTi superconducting composite wire for ITER",

abstract = "This paper shows the results of R&D program carried out to optimize NbTi wires for the Poloidal Field (PF) coils of ITER. The influence of heat treatment on the microstructure was investigated by using TEM to find the relations between the microstructure and the critical current densities at 4.2 K for NbTi superconducting composite wire. Typical microstructure (in transverse cross-section) shows α-Ti pinning centers dispersed within the superconducting β-NbTi matrix with strong fold and curl for the NbTi wire with high critical current density at 4.2 K. It is believed that the higher temperature is beneficial to a higher Jc value at 4.2 K, but the Jc values slightly decrease with increasing the heat treatment times.",

keywords = "Critical current density, ITER, Microstructure, NbTi superconducting wire",

author = "Jianfeng Li and Pingxiang Zhang and Xianghong Liu and Jinshan Li and Yong Feng and Tiancheng Wang and Shejun Du and Weitao Liu and G. Grunblatt and C. Verwaerde and Hoang, {G. K.}",

year = "2009",

month = feb,

language = "英语",

volume = "38",

pages = "263--265",

journal = "Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering",

issn = "1002-185X",

publisher = "Science Press ",

number = "2",

}

TY - JOUR

T1 - Microstructure and properties of NbTi superconducting composite wire for ITER

AU - Li, Jianfeng

AU - Zhang, Pingxiang

AU - Liu, Xianghong

AU - Li, Jinshan

AU - Feng, Yong

AU - Wang, Tiancheng

AU - Du, Shejun

AU - Liu, Weitao

AU - Grunblatt, G.

AU - Verwaerde, C.

AU - Hoang, G. K.

PY - 2009/2

Y1 - 2009/2

N2 - This paper shows the results of R&D program carried out to optimize NbTi wires for the Poloidal Field (PF) coils of ITER. The influence of heat treatment on the microstructure was investigated by using TEM to find the relations between the microstructure and the critical current densities at 4.2 K for NbTi superconducting composite wire. Typical microstructure (in transverse cross-section) shows α-Ti pinning centers dispersed within the superconducting β-NbTi matrix with strong fold and curl for the NbTi wire with high critical current density at 4.2 K. It is believed that the higher temperature is beneficial to a higher Jc value at 4.2 K, but the Jc values slightly decrease with increasing the heat treatment times.

AB - This paper shows the results of R&D program carried out to optimize NbTi wires for the Poloidal Field (PF) coils of ITER. The influence of heat treatment on the microstructure was investigated by using TEM to find the relations between the microstructure and the critical current densities at 4.2 K for NbTi superconducting composite wire. Typical microstructure (in transverse cross-section) shows α-Ti pinning centers dispersed within the superconducting β-NbTi matrix with strong fold and curl for the NbTi wire with high critical current density at 4.2 K. It is believed that the higher temperature is beneficial to a higher Jc value at 4.2 K, but the Jc values slightly decrease with increasing the heat treatment times.

KW - Critical current density

KW - ITER

KW - Microstructure

KW - NbTi superconducting wire

UR - http://www.scopus.com/inward/record.url?scp=65149099615&partnerID=8YFLogxK

M3 - 文章

AN - SCOPUS:65149099615

SN - 1002-185X

VL - 38

SP - 263

EP - 265

JO - Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering

JF - Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering

IS - 2

ER -

Microstructure and properties of NbTi superconducting composite wire for ITER

摘要

其它文件与链接

指纹

引用此