Microstructure and mechanical properties of Al0.7CoCrFeNi high-entropy-alloy prepared by directional solidification

Gang Liu, Lin Liu, Xinwang Liu, Zhijun Wang, Zhenhua Han, Guojun Zhang, A. Kostka

科研成果: 期刊稿件文章同行评审

71 引用 (Scopus)

摘要

The high-entropy-alloy Al0.7CoCrFeNi (molar ratio) was prepared by vacuum arc melting followed by directional solidification (DS) with <001> oriented seed. The unique lamellar-dendrite microstructure was obtained over a wide cooling rate range. During solidification, Fe and Co are prone to segregate to the dendrite, while Cr and Al segregate to interdendrite. The solute pile-up of Cr and Al at the solid/liquid interface leads to the dendritic solidification. During the following cooling process, the BCC phase precipitates from the FCC dendrite to form the lamellar structure, while the ordered B2 phase precipitates from the interdendrite. Moreover, the lamellar spacing is significantly refined with increasing cooling rate, resulting in the higher hardness and compressive yield strength. Directional solidification is proved to be an efficient way to improve the mechanical properties of multi-phases high-entropy alloys.

源语言英语
页(从-至)93-100
页数8
期刊Intermetallics
93
DOI
出版状态已出版 - 2月 2018

指纹

探究 'Microstructure and mechanical properties of Al0.7CoCrFeNi high-entropy-alloy prepared by directional solidification' 的科研主题。它们共同构成独一无二的指纹。

引用此