Microstructure and dielectric properties of Ba0.6Sr0.4TiO3- ZnNb2O6 composite ceramic

Tong Wang; Feng Gao; Guo Xin Hu; Zhen Li; Chang Sheng Tian

Microstructure and dielectric properties of Ba_0.6Sr_0.4TiO₃- ZnNb₂O₆ composite ceramic

Tong Wang, Feng Gao, Guo Xin Hu, Zhen Li, Chang Sheng Tian

材料学院

Northwestern Polytechnical University Xian

科研成果: 期刊稿件 › 文章 › 同行评审

2 引用（Scopus）

摘要

Ba_0.6Sr_0.4TiO₃- ZnNb₂O₆ (BSTZ) composite ceramics were prepared from Ba_0.6Sr_0.4TiO₃ by traditional ceramic processing. The result of XRD, SEM and EDS shows that BSTZ composite ceramics could be sintered at 1200°C, the sintered temperature lower than Ba_0.6Sr_0.4TiO₃, and BaNb_3.6O₁₀ is detected as the secondly phase. With the increasing of ZnNb₂O₆ content, the dielectric constant decrease at 1-100 kHz; the tunabilities of the BSTZ composite ceramics dectease with the increasing of ZnNb₂O₆ content at 1.6 kV/mm.

源语言	英语
页（从-至）	1309-1312
页数	4
期刊	Gongneng Cailiao/Journal of Functional Materials
卷	40
期	8
出版状态	已出版 - 8月 2009

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{270079de5be144a68d7a988748ac1ff6,

title = "Microstructure and dielectric properties of Ba0.6Sr0.4TiO3- ZnNb2O6 composite ceramic",

abstract = "Ba0.6Sr0.4TiO3- ZnNb2O6 (BSTZ) composite ceramics were prepared from Ba0.6Sr0.4TiO3 by traditional ceramic processing. The result of XRD, SEM and EDS shows that BSTZ composite ceramics could be sintered at 1200°C, the sintered temperature lower than Ba0.6Sr0.4TiO3, and BaNb3.6O10 is detected as the secondly phase. With the increasing of ZnNb2O6 content, the dielectric constant decrease at 1-100 kHz; the tunabilities of the BSTZ composite ceramics dectease with the increasing of ZnNb2O6 content at 1.6 kV/mm.",

keywords = "Barium strontium titanate, Dielectric properties, Tunability, Zinc niobium oxide",

author = "Tong Wang and Feng Gao and Hu, {Guo Xin} and Zhen Li and Tian, {Chang Sheng}",

year = "2009",

month = aug,

language = "英语",

volume = "40",

pages = "1309--1312",

journal = "Gongneng Cailiao/Journal of Functional Materials",

issn = "1001-9731",

publisher = "Journal of Functional Materials",

number = "8",

}

TY - JOUR

T1 - Microstructure and dielectric properties of Ba0.6Sr0.4TiO3- ZnNb2O6 composite ceramic

AU - Wang, Tong

AU - Gao, Feng

AU - Hu, Guo Xin

AU - Li, Zhen

AU - Tian, Chang Sheng

PY - 2009/8

Y1 - 2009/8

N2 - Ba0.6Sr0.4TiO3- ZnNb2O6 (BSTZ) composite ceramics were prepared from Ba0.6Sr0.4TiO3 by traditional ceramic processing. The result of XRD, SEM and EDS shows that BSTZ composite ceramics could be sintered at 1200°C, the sintered temperature lower than Ba0.6Sr0.4TiO3, and BaNb3.6O10 is detected as the secondly phase. With the increasing of ZnNb2O6 content, the dielectric constant decrease at 1-100 kHz; the tunabilities of the BSTZ composite ceramics dectease with the increasing of ZnNb2O6 content at 1.6 kV/mm.

AB - Ba0.6Sr0.4TiO3- ZnNb2O6 (BSTZ) composite ceramics were prepared from Ba0.6Sr0.4TiO3 by traditional ceramic processing. The result of XRD, SEM and EDS shows that BSTZ composite ceramics could be sintered at 1200°C, the sintered temperature lower than Ba0.6Sr0.4TiO3, and BaNb3.6O10 is detected as the secondly phase. With the increasing of ZnNb2O6 content, the dielectric constant decrease at 1-100 kHz; the tunabilities of the BSTZ composite ceramics dectease with the increasing of ZnNb2O6 content at 1.6 kV/mm.

KW - Barium strontium titanate

KW - Dielectric properties

KW - Tunability

KW - Zinc niobium oxide

UR - http://www.scopus.com/inward/record.url?scp=70249104659&partnerID=8YFLogxK

M3 - 文章

AN - SCOPUS:70249104659

SN - 1001-9731

VL - 40

SP - 1309

EP - 1312

JO - Gongneng Cailiao/Journal of Functional Materials

JF - Gongneng Cailiao/Journal of Functional Materials

IS - 8

ER -

Microstructure and dielectric properties of Ba0.6Sr0.4TiO3- ZnNb2O6 composite ceramic

摘要

其它文件与链接

指纹

引用此

Microstructure and dielectric properties of Ba_0.6Sr_0.4TiO₃- ZnNb₂O₆ composite ceramic