Microstructural evolution and hydrogen storage proprieties of melt-spun eutectic Mg_76.87Ni_12.78Y_10.35 alloy with low hydrides formation/decomposition enthalpy

Ternary eutectic Mg_76.87Ni_12.78Y_10.35 (at. %) ribbons with mixed amorphous and nanocrystalline phases were prepared by melt spinning. The microstructures of the melt-spun, hydrogenated and dehydrogenated samples were examined and compared by X-ray diffraction and transmission electron microscopy. The amorphous structure transforms into a thermally stable nanocrystalline structure with a grain size of about 5 nm during hydrogen ab/desorption cycles. The Mg, Mg₂Ni and phases with Y in the melt-spun state transform into MgH₂, Mg₂NiH₄, Mg₂NiH_0.3, YH₂ and YH₃ after hydrogenation, and transform back to Mg, Mg₂Ni and YH₂ upon subsequent dehydrogenation. The reaction enthalpy (ΔH) and entropy (ΔS) of the higher plateau pressure corresponding to Mg₂Ni hydride formation are −53.25 kJ mol⁻¹ and −107.74 J K⁻¹ mol⁻¹, respectively. The amorphous/nanocrystalline structure effectively reduces the enthalpy and entropy of Mg₂Ni hydride formation, but has little effect on Mg. The activation energy for dehydrogenation of the hydrogenated ribbons is 69 kJ mol⁻¹. This suggests that Mg–Ni–Y with ternary eutectic composition can form an amorphous/nanocrystalline structure by melt spinning, and this nanostructure efficiently improves the thermodynamics and kinetics for hydrogen storage.