Mechanical and dielectric properties of Al2O3/Ni cermet

Dai Jun Liu, Fa Luo, Peng Li, Dong Mei Zhu, Wan Cheng Zhou

科研成果: 期刊稿件文章同行评审

摘要

Al2O3/Ni cermet were prepared by hot pressing, and the relationship between their microstructure, mechanical and dielectric properties with Ni particle content were investigated. The results show that some Ni particles are slightly elongated in the direction perpendicular to the pressing direction and are arranged in such a-way to form large but finite interconnected clusters which do not span the entire specimen up to a volume fraction higher than 20vol%. By increasing the amount of metal in the cermet, the relative density and the bending strength decreased gradually. For cermet, maximum fracture toughness values were 6.4 MPa·m1/2 which increase 50% of the value for alumina. The complex dielectric constant measurements indicate that the real part and the loss increase greatly with the Ni content in the frequency of 8.2-12.4 GHz. The imaginary part of dielectric constant of Al2O3-20vol%Ni is negative in value within specific frequency because a properly formed, well-bonded network of Nickel actually occurs.

源语言英语
页(从-至)26-28
页数3
期刊Gongneng Cailiao/Journal of Functional Materials
39
1
出版状态已出版 - 1月 2008

指纹

探究 'Mechanical and dielectric properties of Al2O3/Ni cermet' 的科研主题。它们共同构成独一无二的指纹。

引用此