Long-term ceramic matrix composite for aeroengine

Three strategies were proposed to prolong the service life of continuous fiber-reinforced silicon carbide ceramic matrix composite (CMC-SiC), which served as thermal-structure components of aeroengine at thermo-mechanical-oxygenic coupling environment. As for some thermal-structure components with low working stress, improving the degree of densification was crucial to prolong the service life, and the related process approaches were recited. If the thermal-structure components worked under moderate stress, the matrix cracking stress (σ_mc) should be improved as far as possible. The fiber preform architecture, interface shear strength, residual thermal stress, and matrix strengthening were associated with σ_mc in this review. Introducing self-healing components was quite significant with the appearance of matrix microcracks when CMC-SiC worked at more severe environment for hundreds of hours. The damage can be sealed by glass phase originating from the reaction between self-healing components and oxygen. The effective self-healing temperature range of different self-healing components was first summarized and distinguished. The structure, composition, and preparation process of CMC-SiC should be systematically designed and optimized to achieve long duration target. [Figure not available: see fulltext.]