Influence of Packing Atmosphere on the Microstructures and Transport Properties of Bi-2223/AgAu Tapes

Xiaobo Ma, Shengnan Zhang, Zeming Yu, Guoqing Liu, Chengshan Li, Jinshan Li, Pingxiang Zhang

科研成果: 期刊稿件文章同行评审

2 引用 (Scopus)

摘要

Oxygen partial pressure was the key factor to tune the phase evolution mechanism of Bi-2223 system. In order to investigate the influence of packing atmosphere on the phase formation rate of Bi-2223, microstructures‚ and the current capacity of final tapes‚ 37-filamentary Bi-2223/AgAu tapes were fabricated by powder-in-tube (PIT) process, and the powder packing process operated in the glove box under different atmosphere of pure O2‚ air, and N2–7.5%O2, with the oxygen partial pressure of 100%‚ 25%, and 7.5%, respectively. With different packing atmosphere, the phase formation rate of Bi-2223 increased obviously during the first heat treatment process (HT1). While, based on the same HT1 process, the maximum Bi-2223 phase content was obtained in the tapes with packing atmosphere of N2–7.5%O2‚ which should be attributed to the suitable Bi-2223 content and distribution. Due to the improvement of superconducting phase content and better texture structure, the critical current density increased with decreasing oxygen partial pressure of packing atmosphere and the maximum value of 19.9 kA/cm2 was reached. Moreover‚ the in-field current capacities of these Bi-2223/AgAu tapes have also been enhanced with low oxygen partial pressure in packing atmosphere, attributed to the improvements of intergrain connectivity.

源语言英语
页(从-至)2391-2396
页数6
期刊Journal of Superconductivity and Novel Magnetism
32
8
DOI
出版状态已出版 - 15 8月 2019

指纹

探究 'Influence of Packing Atmosphere on the Microstructures and Transport Properties of Bi-2223/AgAu Tapes' 的科研主题。它们共同构成独一无二的指纹。

引用此