Influence of Bi2S3 on the optical properties of γ-La2S3 ceramics

Peisen Li; Wanqi Jie; Huanyong Li; Qingxin Tang; Huan Sha

doi:10.1016/j.scriptamat.2011.02.012

Influence of Bi₂S₃ on the optical properties of γ-La₂S₃ ceramics

Peisen Li, Wanqi Jie, Huanyong Li, Qingxin Tang, Huan Sha

材料学院

Northwestern Polytechnical University Xian

科研成果: 期刊稿件 › 文章 › 同行评审

3 引用（Scopus）

摘要

γ-La₂S₃ ceramics with Bi₂S ₃ as additives were prepared by hot-pressed sintering. The microstructures and optical properties of these ceramics were studied. When the Bi₂S₃ content was 0.1 wt.%, the maximum transmittance was increased from 33% to 45%. Further increase in Bi₂S₃ content decreased the IR transmittance. The existence of Bi phase was the main factor responsible for the difference in transmittance of the pellets with various levels of Bi₂S₃.

源语言	英语
页（从-至）	1023-1026
页数	4
期刊	Scripta Materialia
卷	64
期	11
DOI	https://doi.org/10.1016/j.scriptamat.2011.02.012
出版状态	已出版 - 6月 2011

访问文件

10.1016/j.scriptamat.2011.02.012

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{7c9fcc4a90de4e0fa992a280210a5305,

title = "Influence of Bi2S3 on the optical properties of γ-La2S3 ceramics",

abstract = "γ-La2S3 ceramics with Bi2S 3 as additives were prepared by hot-pressed sintering. The microstructures and optical properties of these ceramics were studied. When the Bi2S3 content was 0.1 wt.%, the maximum transmittance was increased from 33% to 45%. Further increase in Bi2S3 content decreased the IR transmittance. The existence of Bi phase was the main factor responsible for the difference in transmittance of the pellets with various levels of Bi2S3.",

keywords = "Ceramics, Fracture, Hot pressing, Optical properties, Rare earth",

author = "Peisen Li and Wanqi Jie and Huanyong Li and Qingxin Tang and Huan Sha",

year = "2011",

month = jun,

doi = "10.1016/j.scriptamat.2011.02.012",

language = "英语",

volume = "64",

pages = "1023--1026",

journal = "Scripta Materialia",

issn = "1359-6462",

publisher = "Acta Materialia Inc",

number = "11",

}

TY - JOUR

T1 - Influence of Bi2S3 on the optical properties of γ-La2S3 ceramics

AU - Li, Peisen

AU - Jie, Wanqi

AU - Li, Huanyong

AU - Tang, Qingxin

AU - Sha, Huan

PY - 2011/6

Y1 - 2011/6

N2 - γ-La2S3 ceramics with Bi2S 3 as additives were prepared by hot-pressed sintering. The microstructures and optical properties of these ceramics were studied. When the Bi2S3 content was 0.1 wt.%, the maximum transmittance was increased from 33% to 45%. Further increase in Bi2S3 content decreased the IR transmittance. The existence of Bi phase was the main factor responsible for the difference in transmittance of the pellets with various levels of Bi2S3.

AB - γ-La2S3 ceramics with Bi2S 3 as additives were prepared by hot-pressed sintering. The microstructures and optical properties of these ceramics were studied. When the Bi2S3 content was 0.1 wt.%, the maximum transmittance was increased from 33% to 45%. Further increase in Bi2S3 content decreased the IR transmittance. The existence of Bi phase was the main factor responsible for the difference in transmittance of the pellets with various levels of Bi2S3.

KW - Ceramics

KW - Fracture

KW - Hot pressing

KW - Optical properties

KW - Rare earth

UR - http://www.scopus.com/inward/record.url?scp=79953066188&partnerID=8YFLogxK

U2 - 10.1016/j.scriptamat.2011.02.012

DO - 10.1016/j.scriptamat.2011.02.012

M3 - 文章

AN - SCOPUS:79953066188

SN - 1359-6462

VL - 64

SP - 1023

EP - 1026

JO - Scripta Materialia

JF - Scripta Materialia

IS - 11

ER -

Influence of Bi2S3 on the optical properties of γ-La2S3 ceramics

摘要

访问文件

其它文件与链接

指纹

引用此

Influence of Bi₂S₃ on the optical properties of γ-La₂S₃ ceramics