In situ synthesis of Ti3SiC2/SiC composite by displacement reaction of Si and TiC

Shi Bo Li, Jian Xin Xie, Li Tong Zhang, Lai Fei Cheng

科研成果: 期刊稿件文章同行评审

55 引用 (Scopus)

摘要

In situ synthesis technology was adopted to fabricate SiC reinforced Ti3SiC2 composite by displacement reaction of Si and TiC powders. The formation of SiC particles as reinforcements with elongated or equiaxed shape distributed in Ti3SiC2 matrix. The average size of SiC equiaxed particles was about 2 μm and that of elongated ones was in the range of 5-8 μm in length and 2 μm in width. TiC with about 1 μm in size was also found in the composite. The particles of SiC or TiC inhibited the grain-boundary migration of Ti3SiC2 resulting in a fine Ti3SiC2 matrix with a grain size of 10 μm. Differential scanning calorimetry showed that Si reacted drastically with TiC at 1340 °C with release of heat. The presence of TiC in the Ti3SiC2/SiC composite should be attributed to decomposition of Ti3SiC2 at 1500 °C rather than the loss of Si during reaction process that resulted in unreacted TiC left. Reaction paths in the present experiment were postulated on the basis of Ti-Si-C system and reaction model of Mo2C-Si to understand the mechanism of the formation of Ti3SiC2 and SiC.

源语言英语
页(从-至)51-56
页数6
期刊Materials Science and Engineering: A
381
1-2
DOI
出版状态已出版 - 15 9月 2004

指纹

探究 'In situ synthesis of Ti3SiC2/SiC composite by displacement reaction of Si and TiC' 的科研主题。它们共同构成独一无二的指纹。

引用此