In-situ formation of Ti₃SiC₂ interphase in SiC_f/SiC composites by molten salt synthesis

Titanium silicon carbide (Ti₃SiC₂) film was synthesized by molten salt synthesis route of titanium and silicon powder based on polymer-derived SiC fibre substrate. The pre-deposited pyrolytic carbon (PyC) coating on the fibre was utilized as the template and a reactant for Ti₃SiC₂ film. The morphology, microstructure and composition of the film product were characterized. Two Ti₃SiC₂ layers form the whole film, where the Ti₃SiC₂ grains have different features. The synthesis mechanism has been discussed from the thickness of PyC and the batching ratio of mixed powder respectively. Finally, the obtained Ti₃SiC₂ film was utilized as interphase to prepare the SiC fibre reinforced SiC matrix composites (SiC_f/Ti₃SiC₂/SiC composites). The flexural strength (σ_F) and fracture toughness (K_IC) of the SiC_f/Ti₃SiC₂/SiC composite is 460 ± 20 MPa and 16.8 ± 2.4 MPa∙m^1/2 respectively.