Enhanced energy-storage properties of (1-x)(0.7Bi_0.5Na_0.5TiO₃-0.3Bi_0.2Sr_0.7TiO₃)-xNaNbO₃ lead-free ceramics

A series of (1-x)(0.7Bi_0.5Na_0.5TiO₃-0.3Bi_0.2Sr_0.7TiO₃)-xNaNbO₃ (BNT-BST-100xNN) lead-free ceramics were fabricated using conventional solid-state reaction technique. The phase behavior, microstructure, dielectric, ac impedance and energy-storage properties of the sintered ceramics were systematically investigated. XRD patterns and surface SEM micrographs revealed the introduction of NaNbO₃ didn't change the perovskite structure of BNT-BST at low doping level. The NaNbO₃ doping gave rise to slimmer P-E loops and thus gained enhanced energy storage properties. Therefore, a maximum energy storage density of 1.03 J/cm³ was achieved at 85 kV/cm at x = 0.01 via increasing the dielectric breakdown strength (DBS). Temperature-dependent dielectric permittivity illustrated the enhanced relaxor characteristics, implying the long-rang ferroelectric order was further damaged due to the introduction of NaNbO₃. The results above indicate the sintered ternary ceramics can be a promising lead-free candidate for energy storage capacitors.