Effect of temperature gradient on the ablation and flexural behavior of C/C-ZrC composites

Tianyu Liu; Qiangang Fu; Bing Liu; Jiaping Zhang

doi:10.1016/j.corsci.2021.109736

Effect of temperature gradient on the ablation and flexural behavior of C/C-ZrC composites

Tianyu Liu, Qiangang Fu, Bing Liu, Jiaping Zhang

材料学院

Northwestern Polytechnical University Xian

科研成果: 期刊稿件 › 文章 › 同行评审

32 引用（Scopus）

摘要

A new ablation condition was designed to investigate the effect of temperature gradient on the ablation and flexural behavior of the C/C-ZrC composites. The sample not only suffers the gradient temperature ablation ranging from 1000 to 2000 ℃ but withstands flexural load caused by the high-speed airflow scouring. The volume ablation rate of the C/C-ZrC was 0.06 mm³/s, which was only 6.81 % of the rate of the C/C. The volume change caused by ZrC→ZrO₂ together with the ZrO₂ crystalline transformation was beneficial for releasing internal stress, thereby contributing to the higher flexural strength retention of the C/C-ZrC composites.

源语言	英语
文章编号	109736
期刊	Corrosion Science
卷	191
DOI	https://doi.org/10.1016/j.corsci.2021.109736
出版状态	已出版 - 10月 2021

访问文件

10.1016/j.corsci.2021.109736

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{3e6bacd0f3bd409c994c9a83d1521757,

title = "Effect of temperature gradient on the ablation and flexural behavior of C/C-ZrC composites",

abstract = "A new ablation condition was designed to investigate the effect of temperature gradient on the ablation and flexural behavior of the C/C-ZrC composites. The sample not only suffers the gradient temperature ablation ranging from 1000 to 2000 ℃ but withstands flexural load caused by the high-speed airflow scouring. The volume ablation rate of the C/C-ZrC was 0.06 mm3/s, which was only 6.81 % of the rate of the C/C. The volume change caused by ZrC→ZrO2 together with the ZrO2 crystalline transformation was beneficial for releasing internal stress, thereby contributing to the higher flexural strength retention of the C/C-ZrC composites.",

keywords = "C/C-ZrC composites, Flexural strength, Gradient ablation",

author = "Tianyu Liu and Qiangang Fu and Bing Liu and Jiaping Zhang",

note = "Publisher Copyright: {\textcopyright} 2021 Elsevier Ltd",

year = "2021",

month = oct,

doi = "10.1016/j.corsci.2021.109736",

language = "英语",

volume = "191",

journal = "Corrosion Science",

issn = "0010-938X",

publisher = "Elsevier Ltd",

}

TY - JOUR

T1 - Effect of temperature gradient on the ablation and flexural behavior of C/C-ZrC composites

AU - Liu, Tianyu

AU - Fu, Qiangang

AU - Liu, Bing

AU - Zhang, Jiaping

PY - 2021/10

Y1 - 2021/10

N2 - A new ablation condition was designed to investigate the effect of temperature gradient on the ablation and flexural behavior of the C/C-ZrC composites. The sample not only suffers the gradient temperature ablation ranging from 1000 to 2000 ℃ but withstands flexural load caused by the high-speed airflow scouring. The volume ablation rate of the C/C-ZrC was 0.06 mm3/s, which was only 6.81 % of the rate of the C/C. The volume change caused by ZrC→ZrO2 together with the ZrO2 crystalline transformation was beneficial for releasing internal stress, thereby contributing to the higher flexural strength retention of the C/C-ZrC composites.

AB - A new ablation condition was designed to investigate the effect of temperature gradient on the ablation and flexural behavior of the C/C-ZrC composites. The sample not only suffers the gradient temperature ablation ranging from 1000 to 2000 ℃ but withstands flexural load caused by the high-speed airflow scouring. The volume ablation rate of the C/C-ZrC was 0.06 mm3/s, which was only 6.81 % of the rate of the C/C. The volume change caused by ZrC→ZrO2 together with the ZrO2 crystalline transformation was beneficial for releasing internal stress, thereby contributing to the higher flexural strength retention of the C/C-ZrC composites.

KW - C/C-ZrC composites

KW - Flexural strength

KW - Gradient ablation

UR - http://www.scopus.com/inward/record.url?scp=85113646964&partnerID=8YFLogxK

U2 - 10.1016/j.corsci.2021.109736

DO - 10.1016/j.corsci.2021.109736

M3 - 文章

AN - SCOPUS:85113646964

SN - 0010-938X

VL - 191

JO - Corrosion Science

JF - Corrosion Science

M1 - 109736

ER -

Effect of temperature gradient on the ablation and flexural behavior of C/C-ZrC composites

摘要

访问文件

其它文件与链接

指纹

引用此