Effect of solutionising and ageing on the microstructure and mechanical properties of a high strength die-cast Al-Mg-Zn-Si alloy

Feng Yan, Wenchao Yang, Shouxun Ji, Zhongyun Fan

科研成果: 期刊稿件文章同行评审

26 引用 (Scopus)

摘要

Solutionising and ageing heat treatment for a newly developed die-cast Al-Mg-Zn-Si alloy has been carried out in order to investigate the microstructural evolution, the improvement in mechanical properties and the relevant strengthening mechanisms. Based on the results obtained from the treatment at different temperatures and periods of time, the heat treatment was optimised to be at 490 °C for 30 min for the solutionising, and at 180 °C for 60 min for the ageing by considering the improvement of both the strength and ductility. Mg32(Al,Zn)49 intermetallic in the as-cast microstructure was dissolved into the α-Al phase during solutionising and fine precipitates were formed during the subsequent ageing to enhance the mechanical properties of the alloy. After the heat treatment, the samples made by high pressure die-casting exhibited yield strength of 320 MPa, UTS of 420 MPa and elongation of 4.5%, which was a significant improvement in comparison with that under as-cast condition. The improvement of the mechanical properties achieved by the solution and ageing treatment is favourable for the applications where lightweight and high strength are essential for structural thin wall castings.

源语言英语
页(从-至)88-96
页数9
期刊Materials Chemistry and Physics
167
DOI
出版状态已出版 - 1 11月 2015
已对外发布

指纹

探究 'Effect of solutionising and ageing on the microstructure and mechanical properties of a high strength die-cast Al-Mg-Zn-Si alloy' 的科研主题。它们共同构成独一无二的指纹。

引用此