Effect of platelet template seeds on microstructure and thermoelectric properties of Ca3Co4O9 ceramics

Zongmo Shi, Jie Xu, Jihong Zhu, Yi Zhang, Tong Gao, Mengjie Qin, Han Sun, Gaogao Dong, Feng Gao

科研成果: 期刊稿件文章同行评审

34 引用 (Scopus)

摘要

Plate-like Ca3Co4O9 microcrystal particles were synthesized by molten salt synthesis. Denser Ca3Co4O9 thermoelectric ceramics were fabricated by utilizing morphologically optimized particles as the template seeds. Effects of Ca3Co4O9 template seeds on microstructure and thermoelectric properties of ceramics were investigated. The results showed that weight ratios of salt to oxides (s/o) had great influence on components, microstructure, and grain size of template seeds. The particles displayed satisfactory morphology and uniform grain size when the ratio of s/o reached 1, with a mean grain size of 7.92 µm in diameter and 1.13 µm in thickness. The bulk density of Ca3Co4O9 ceramics was 92.5% in the presence of 40 wt% of the template seed. The thermoelectric properties were measured from 50 °C to 800 °C. The results showed an electrical resistivity of 20.3 mΩ cm, a Seebeck coefficient of 179 μV/K and a power factor of 0.16 mW/m K2. The ZT value can reach 0.15 at 800 °C, which is 1.6 times higher than that of conventional Ca3Co4O9 thermoelectric ceramics.

源语言英语
页(从-至)1977-1983
页数7
期刊Ceramics International
45
2
DOI
出版状态已出版 - 1 2月 2019

指纹

探究 'Effect of platelet template seeds on microstructure and thermoelectric properties of Ca3Co4O9 ceramics' 的科研主题。它们共同构成独一无二的指纹。

引用此