Effect factors on thermal and mechanical properties of SiO2 and TiB2 modified SiBCN-based adhesives

Xin'gang Luan, Min Li, Sen Chang, Yongguo Li, Kunjun Wang, Xuemei Song, Ralf Riedel, Laifei Cheng

科研成果: 期刊稿件文章同行评审

14 引用 (Scopus)

摘要

To further investigate the reinforcing factors on the adhesion strength of SiO2 and TiB2 modified SiBCN-based adhesives, the thermal stability analysis, microstructure observations and phase composition analysis were performed on four kinds of modified PSNB (Polyborosilazane) adhesives. With the different Si/B ratio and SiO2 content, the room temperature adhesion strength reach up to 18.95, 12.04, 32.44 and 13.69 MPa for PPT-1, PPT-2, PPTS and PST respectively, after synthesized at 1000 °C in air. And then, the high temperature adhesion strength reach up to 12.3 and 16.4 MPa for PPT-1 and PPTS at 1000 °C in vacuum, respectively. Interestingly, it has been found that temperature, PSO, solid content and SiO2 content all have a great influence on the adhesion performance of SiO2 and TiB2 modified SiBCN-based adhesives.

源语言英语
页(从-至)19416-19424
页数9
期刊Ceramics International
46
11
DOI
出版状态已出版 - 1 8月 2020

指纹

探究 'Effect factors on thermal and mechanical properties of SiO2 and TiB2 modified SiBCN-based adhesives' 的科研主题。它们共同构成独一无二的指纹。

引用此