Damage evolution and microstructural characterization of a cross-woven C/SiC composite under tensile loading

Engineering

• Damage Evolution 100%
• Tensiles 100%
• Damage Behavior 100%
• Failure Strain 50%
• Mechanical Response 50%
• Delamination 50%
• Fracture Strength 50%
• Acoustic Emission 50%
• Interfacial Debonding 50%
• Damage Accumulation 50%
• Fracture Failure 50%
• Microcracking 50%
• Stress-Strain Relations 50%
• Fiber Fracture 50%
• Mechanical Loading 50%