Combustion synthesis and characterization of Fe-ni alloys1

Y. H. Kang; L. Wang; L. C. Fu; J. Yang; Q. L. Bi; W. M. Liu

doi:10.3103/S1061386211020099

Combustion synthesis and characterization of Fe-ni alloys1

Y. H. Kang, L. Wang, L. C. Fu, J. Yang, Q. L. Bi, W. M. Liu

科研成果: 期刊稿件 › 文章 › 同行评审

3 引用（Scopus）

摘要

A simple and inexpensive method for combustion synthesis of the series of Fe-x%Ni martensite alloys (x = 15, 20, 23, 25 at %) was developed. XRD, SEM, and TEM examinations showed that all the prod- ucts were composed of lath martensite and retained austenite. With increasing nickel content, the hardness and yield strength decreased gradually, which originated from the differences in phase compositions and micro structural characteristics. All the products exhibited high strength and good ductility, especially the Fe-15%Ni alloy which exhibited (in compression tests) high yield strength (up to 1300 MPa) at a good duc- tility (∼30%).

源语言	英语
页（从-至）	134-139
页数	6
期刊	International Journal of Self-Propagating High-Temperature Synthesis
卷	20
期	2
DOI	https://doi.org/10.3103/S1061386211020099
出版状态	已出版 - 6月 2011
已对外发布	是

访问文件

10.3103/S1061386211020099

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{bef9c9adc105470c9118e92f9da0e672,

title = "Combustion synthesis and characterization of Fe-ni alloys1",

abstract = "A simple and inexpensive method for combustion synthesis of the series of Fe-x%Ni martensite alloys (x = 15, 20, 23, 25 at %) was developed. XRD, SEM, and TEM examinations showed that all the prod- ucts were composed of lath martensite and retained austenite. With increasing nickel content, the hardness and yield strength decreased gradually, which originated from the differences in phase compositions and micro structural characteristics. All the products exhibited high strength and good ductility, especially the Fe-15%Ni alloy which exhibited (in compression tests) high yield strength (up to 1300 MPa) at a good duc- tility (∼30%).",

keywords = "Combustion synthesis, Fe-Ni alloys, Martensite, Retained austenite",

author = "Kang, {Y. H.} and L. Wang and Fu, {L. C.} and J. Yang and Bi, {Q. L.} and Liu, {W. M.}",

year = "2011",

month = jun,

doi = "10.3103/S1061386211020099",

language = "英语",

volume = "20",

pages = "134--139",

journal = "International Journal of Self-Propagating High-Temperature Synthesis",

issn = "1061-3862",

publisher = "Pleiades Publishing",

number = "2",

}

TY - JOUR

T1 - Combustion synthesis and characterization of Fe-ni alloys1

AU - Kang, Y. H.

AU - Wang, L.

AU - Fu, L. C.

AU - Yang, J.

AU - Bi, Q. L.

AU - Liu, W. M.

PY - 2011/6

Y1 - 2011/6

N2 - A simple and inexpensive method for combustion synthesis of the series of Fe-x%Ni martensite alloys (x = 15, 20, 23, 25 at %) was developed. XRD, SEM, and TEM examinations showed that all the prod- ucts were composed of lath martensite and retained austenite. With increasing nickel content, the hardness and yield strength decreased gradually, which originated from the differences in phase compositions and micro structural characteristics. All the products exhibited high strength and good ductility, especially the Fe-15%Ni alloy which exhibited (in compression tests) high yield strength (up to 1300 MPa) at a good duc- tility (∼30%).

AB - A simple and inexpensive method for combustion synthesis of the series of Fe-x%Ni martensite alloys (x = 15, 20, 23, 25 at %) was developed. XRD, SEM, and TEM examinations showed that all the prod- ucts were composed of lath martensite and retained austenite. With increasing nickel content, the hardness and yield strength decreased gradually, which originated from the differences in phase compositions and micro structural characteristics. All the products exhibited high strength and good ductility, especially the Fe-15%Ni alloy which exhibited (in compression tests) high yield strength (up to 1300 MPa) at a good duc- tility (∼30%).

KW - Combustion synthesis

KW - Fe-Ni alloys

KW - Martensite

KW - Retained austenite

UR - http://www.scopus.com/inward/record.url?scp=80052629129&partnerID=8YFLogxK

U2 - 10.3103/S1061386211020099

DO - 10.3103/S1061386211020099

M3 - 文章

AN - SCOPUS:80052629129

SN - 1061-3862

VL - 20

SP - 134

EP - 139

JO - International Journal of Self-Propagating High-Temperature Synthesis

JF - International Journal of Self-Propagating High-Temperature Synthesis

IS - 2

ER -

Combustion synthesis and characterization of Fe-ni alloys1

摘要

访问文件

其它文件与链接

指纹

引用此