Behavior and mechanism of flame retardant epoxy resins with intrinsic phosphorus-nitrogen phenolic resin curing agents

Lailai Yuan, Zhi Yang, Panjin Zeng, Tong Gao, Yuelin Lv, Xiaochen Liu, Ye Ou, Lixin Chen

科研成果: 期刊稿件文章同行评审

14 引用 (Scopus)

摘要

In this paper, two phosphorus-nitrogen phenolic resins (DPO-PR, DOPO-PR) were synthesized from phenol, paraformaldehyde, dicyandiamide, DOPO, and diphenylphosphine oxide (DPO) as raw materials as curing agents and were applied in epoxy resins. The structures of DPO-PR and DOPO-PR were characterized by FTIR, 1H NMR and 31P NMR. In the TGA test, the decomposition temperature of DPO-PR/EP and DOPO-PR/EP decreased, but the residue yield increased substantially. DPO-PR/EP had a higher LOI value than DOPO-PR/EP at the same addition amount. Compared with PR/EP, DPO-PR/EP showed that pk-HRR decreased by 41.5 %, THR decreased by 29.4 %, and a slight increase in residue yield. DPO-PR/EP and DOPO-PR/EP were analyzed by TG-MS, and the results showed that both DPO-PR/EP and DOPO-PR/EP can decompose phosphorus free radicals to exert quenching effects. Characterization of the char layer by SEM and XPS showed that DPO-PR and DOPO-PR were able to produce phosphoric acid substances to promote the dehydration of the epoxy resin into char layer, enhance the integrity of the char layer of the epoxy resin, and effectively exert the shielding and barrier effect.

源语言英语
文章编号112959
期刊European Polymer Journal
210
DOI
出版状态已出版 - 24 4月 2024

指纹

探究 'Behavior and mechanism of flame retardant epoxy resins with intrinsic phosphorus-nitrogen phenolic resin curing agents' 的科研主题。它们共同构成独一无二的指纹。

引用此