Analysis and prediction of non-isothermal creep behavior in Ni-based single crystal superalloy

Jian Wei Liang, Jia Po Wang, Zhi Xun Wen, Zhu Feng Yue

科研成果: 期刊稿件文章同行评审

16 引用 (Scopus)

摘要

Non-isothermal creep tests have been performed on single crystal superalloy to investigate the effect of the temperature change on creep behavior. Creep tests were carried out under constant load σ0 = 300 MPa using a changing temperature route: 980 °C–1050 °C–980 °C. The pre-creep time is designed as 5 h, 10 h and 15 h. The non-isothermal temperature is set at 1050 °C and maintains 30 min. The results show that longer pre-creep time tpre generates larger strain rate after temperature change, therefore, the creep life is shorter. Moreover, creep strain jump can be observed with the rise of temperature, a new primary and secondary stage can be found. In view of these phenomena, this paper pays remarkable attention on the evolution of the microstructure at the positions where the temperature changes. To predict the non-isothermal creep behavior, a modified crystal plasticity model was proposed by adding physically motivated internal variables, e.g. dislocation density and matrix channel width. The non-isothermal creep behavior predicted by finite element calculation was in a good agreement with the experimental results.

源语言英语
页(从-至)559-566
页数8
期刊Materials Science and Engineering: A
707
DOI
出版状态已出版 - 7 11月 2017

指纹

探究 'Analysis and prediction of non-isothermal creep behavior in Ni-based single crystal superalloy' 的科研主题。它们共同构成独一无二的指纹。

引用此