石墨烯强化铜铌复合线材的研究

Pengfei Wang, Ming Liang, Xiaoyan Xu, Lihua Jin, Jianqing Feng, Chengshan Li, Jinshan Li, Pingxiang Zhang

科研成果: 期刊稿件文章同行评审

摘要

Cu-Nb was reinforced by graphene coated niobium powder and pure niobium powder to prepare Cu-Nb-C microcomposite 73 filaments and Cu-Nb microcomposite 73 filaments by powder casing method and bundle-drawing technology. Through the characterization of filaments configuration and the microstructure of two kinds of wires, it is found the filaments distribution with introduction of graphene doping is relatively regular and uniform, due to the lubricating property of graphene well coordinating the deformation between Cu matrix and Nb filaments. Through the analysis of mechanical properties and electrical conductivity of two wires with different sizes, the results show that the strength of Cu-Nb-C wires increases with only tens of MPa compared with Cu-Nb wires, however, the conductivity of the Cu-Nb-C wire increases obviously, which reaches 9%. The excellent properties of graphene itself and the uniform distribution of filaments are the main reasons for the improvement of conductivity, which may provide theoretical basis and experimental basis for the development of a new generation of high-strength and high-conductivity Cu-Nb composite wires.

投稿的翻译标题Research on the Cu-Nb Microcomposites Reinforced by Graphene
源语言繁体中文
页(从-至)1082-1085
页数4
期刊Materials China
38
11
DOI
出版状态已出版 - 1 11月 2019

关键词

  • Conductive mechanism
  • Cu-Nb composite wire
  • Graphene
  • Mechanical properties
  • Microstructure

指纹

探究 '石墨烯强化铜铌复合线材的研究' 的科研主题。它们共同构成独一无二的指纹。

引用此