@inproceedings{2b228c37ba084648bc6e1191e42cd7f0,
title = "The effect of SiC coating on the joint of C/C and LAS",
abstract = "The SiC coating on C/C composites was prepared by CVD and pack-cementation method in this paper, then SiC coated C/C composites was jointed with LAS glass ceramic at 1423K for 30min and the pressure of 15 MPa. The structure and morphology of the SiC coating and as-received joints were analyzed by SEM and XRD; shear strength of joint was examined through the Instron universal testing tensile machine. The results show that the thickness of SiC coating prepared by CVD is about 30μm, while the thickness of SiC layer by pack-cementation is nearly 100μm, and the layer is easier to connect with LAS glass ceramic owing to the rough surface and wedge-shaped structure on the SiC coating; the shear strength of joint between SiC coating coated C/C and LAS by pack-cementation is greater than the joint of C/C- LAS with SiC coating prepared by CVD.",
keywords = "C/C composites, Joint, SiC coating",
author = "Huanxia Zhu and Kezhi Li and Jinhua Lu and Hejun Li",
year = "2013",
doi = "10.4028/www.scientific.net/KEM.537.24",
language = "英语",
isbn = "9783037855669",
series = "Key Engineering Materials",
publisher = "Trans Tech Publications Ltd",
pages = "24--27",
booktitle = "Inorganic Thin Films and Coatings",
note = "2012 Workshop on Inorganic Thin Films and Coatings ; Conference date: 16-07-2012 Through 18-07-2012",
}