Effect of deposition pressure on microstructure and properties of hydrogenated carbon nitride films prepared by DC-RF-PECVD

Hydrogenated carbon nitride (a-CN:H films) were deposited on n-type (1 0 0) silicon substrates making use of dual direct current radio frequency plasma enhanced chemical vapor deposition (DC-RF-PECVD), at working pressure of 2-20 Pa, using a mixed gas of CH₄ and N₂ as the source gas. The growth rate, composition, bonding structure of the deposited films were characterized by means of XPS and FTIR, and the mechanical properties of the deposited films were investigated by nano-indentation test. It was found that the parameters for the DC-RF-PECVD process had significant effects on the growth rate, structure and properties of the deposited films. The growth rate of the deposited films increased at first with increasing deposition pressure, then saturated with further increase of the deposition pressure. The N/C ratio inside the deposited films increased with increasing working pressure except that it was as much as 0.50 at a working pressure of 5.0 Pa. The nano-hardness of the films decreased with increasing deposition pressure. CN radicals were remarkably formed in the deposited films at higher pressures, and their contents are related to the nitrogen concentrations in the deposited films.