TY - JOUR
T1 - Comparison of precipitated calcium carbonate/polylactic acid and halloysite/polylactic acid nanocomposites
AU - Shi, Xuetao
AU - Zhang, Guangcheng
AU - Siligardi, Cristina
AU - Ori, Guido
AU - Lazzeri, Andrea
N1 - Publisher Copyright:
© 2015 Xuetao Shi et al.
PY - 2015/2/28
Y1 - 2015/2/28
N2 - PLA nanocomposites with stearate coated precipitated calcium carbonate (PCC) and halloysite natural nanotubes (HNT) were prepared by melt extrusion. The crystallization behavior, mechanical properties, thermal dynamical mechanical analysis (DMTA), and the morphology of the PCC/PLA, HNT/PLA, and HNT/PCC/PLA composites were discussed. Compared to halloysite nanotubes, PCC nanoparticles showed a better nucleating effect, which decreased both the glass transition and cold crystallization temperatures. The tensile performance of PLA composites showed that the addition of inorganic nanofillers increased Young's modulus but decreased tensile strength. More interestingly, PLA composites with PCC particles exhibited an effectively increased elongation at break with respect to pure PLA, while HNT/PLA showed a decreased ultimate deformation of composites. DMTA results indicated that PLA composites had a similar storage modulus at temperatures below the glass transition and the addition of nanofillers into PLA caused T g to shift to lower temperatures by about 3°C. The morphological analysis of fractures surface of PLA nanocomposites showed good dispersion of nanofillers, formation of microvoids, and larger plastic deformation of the PLA matrix when the PCC particles were added, while a strong aggregation was noticed in composites with HNT nanofillers, which has been attributed to a nonoptimal surface coating.
AB - PLA nanocomposites with stearate coated precipitated calcium carbonate (PCC) and halloysite natural nanotubes (HNT) were prepared by melt extrusion. The crystallization behavior, mechanical properties, thermal dynamical mechanical analysis (DMTA), and the morphology of the PCC/PLA, HNT/PLA, and HNT/PCC/PLA composites were discussed. Compared to halloysite nanotubes, PCC nanoparticles showed a better nucleating effect, which decreased both the glass transition and cold crystallization temperatures. The tensile performance of PLA composites showed that the addition of inorganic nanofillers increased Young's modulus but decreased tensile strength. More interestingly, PLA composites with PCC particles exhibited an effectively increased elongation at break with respect to pure PLA, while HNT/PLA showed a decreased ultimate deformation of composites. DMTA results indicated that PLA composites had a similar storage modulus at temperatures below the glass transition and the addition of nanofillers into PLA caused T g to shift to lower temperatures by about 3°C. The morphological analysis of fractures surface of PLA nanocomposites showed good dispersion of nanofillers, formation of microvoids, and larger plastic deformation of the PLA matrix when the PCC particles were added, while a strong aggregation was noticed in composites with HNT nanofillers, which has been attributed to a nonoptimal surface coating.
UR - http://www.scopus.com/inward/record.url?scp=84924390188&partnerID=8YFLogxK
U2 - 10.1155/2015/905210
DO - 10.1155/2015/905210
M3 - 文章
AN - SCOPUS:84924390188
SN - 1687-4110
VL - 2015
JO - Journal of Nanomaterials
JF - Journal of Nanomaterials
M1 - 905210
ER -