T1 - Calcia-doped ceria hybrid coating functionalized PBO fibers with excellent UV resistance and improved interfacial compatibility with cyanate ester resins
AU - Tang, Lin
AU - Fan, Xiaoli
AU - Tang, Yusheng
AU - Zhang, Junliang
AU - Kong, Jie
AU - Gu, Junwei
N1 - Publisher Copyright:
© 2021 Elsevier B.V.
PY - 2021/12/15
Y1 - 2021/12/15
N2 - Poly(p-phenylene-2,6-benzobisoxazole) (PBO) fibers display weak outdoor stability and reliability due to their poor UV resistance and chemically inert surface. In this work, calcia-doped ceria (Ce0.8Ca0.2O1.8) nanoparticles was fabricated via chemical co-precipitation method, and the novel Ce0.8Ca0.2O1.8/P(S-co-BCB-co-MMA) organic–inorganic hybrid coating was then designed and prepared for surface functionalization of PBO fibers (PBO@P-Ce0.8Ca0.2O1.8). Organic-inorganic hybrid coating presents high surface roughness and excellent UV resistance. When the concentration of Ce0.8Ca0.2O1.8 nanoparticles with the particle size of about 50 nm is 0.6 wt%, PBO@P-Ce0.8Ca0.2O1.8–3 fibers (sample 4, 0.6 wt%) present the best interfacial bonding strength with modified bisphenol A cyanate (BADCy) resins, the single fiber pull-out strength between sample 4 and modified BADCy resins reaches the maximum value of 4.6 MPa, 48.4% higher than that of pristine PBO fibers (sample 0, 3.1 MPa). Meanwhile, the tensile strength of sample 4 after 288 h UV aging is increased from 1.4 GPa (PBO fibers) to 4.1 GPa. Overall, functionalized PBO fibers in this work demonstrate higher surface activity, excellent UV resistance and improved interfacial bonding strength with modified BADCy resins, which provides a new idea for functionalizing the surface activity and UV resistance of high-performance polymer fibers.
AB - Poly(p-phenylene-2,6-benzobisoxazole) (PBO) fibers display weak outdoor stability and reliability due to their poor UV resistance and chemically inert surface. In this work, calcia-doped ceria (Ce0.8Ca0.2O1.8) nanoparticles was fabricated via chemical co-precipitation method, and the novel Ce0.8Ca0.2O1.8/P(S-co-BCB-co-MMA) organic–inorganic hybrid coating was then designed and prepared for surface functionalization of PBO fibers (PBO@P-Ce0.8Ca0.2O1.8). Organic-inorganic hybrid coating presents high surface roughness and excellent UV resistance. When the concentration of Ce0.8Ca0.2O1.8 nanoparticles with the particle size of about 50 nm is 0.6 wt%, PBO@P-Ce0.8Ca0.2O1.8–3 fibers (sample 4, 0.6 wt%) present the best interfacial bonding strength with modified bisphenol A cyanate (BADCy) resins, the single fiber pull-out strength between sample 4 and modified BADCy resins reaches the maximum value of 4.6 MPa, 48.4% higher than that of pristine PBO fibers (sample 0, 3.1 MPa). Meanwhile, the tensile strength of sample 4 after 288 h UV aging is increased from 1.4 GPa (PBO fibers) to 4.1 GPa. Overall, functionalized PBO fibers in this work demonstrate higher surface activity, excellent UV resistance and improved interfacial bonding strength with modified BADCy resins, which provides a new idea for functionalizing the surface activity and UV resistance of high-performance polymer fibers.
KW - Interfacial bonding strength
KW - Organic-inorganic hybrid coating
KW - PBO fibers
KW - UV resistance
UR - http://www.scopus.com/inward/record.url?scp=85113924989&partnerID=8YFLogxK
U2 - 10.1016/j.apsusc.2021.151124
DO - 10.1016/j.apsusc.2021.151124
M3 - 文章
AN - SCOPUS:85113924989
SN - 0169-4332
VL - 569
JO - Applied Surface Science
JF - Applied Surface Science
M1 - 151124
ER -