Undercooled solidification of Ni-3?3 wt-%B alloy and cooling curve description

Undercooled solidification of hypoeutectic Ni-3?3 wt-%B alloy has been studied. The microstructure evolution of Ni-3?3 wt-%B alloy indicates that a transition from regular lamellar eutectic to anomalous eutectic exists with increasing undercooling for eutectic transformation. Here, a new model was proposed to describe the cooling curves of undercooled solidification with two-step transformation. Fits of the present model to the cooling curves after different undercoolings show that the predictions of transformed fractions are compatible with the microstructure observation. Furthermore, for hypoeutectic alloy, the size of the primary phase mainly depends on the undercooling for primary solidification, while the fraction of the primary phase mainly depends on the undercooling for eutectic solidification.