The influence of microstructure on dwell sensitive fatigue in Ti-6.5Al-3.5Mo-1.5Zr-0.3Si alloy

The fatigue behaviour of titanium alloy Ti-6.5Al-3.5Mo-1.5Zr-0.3Si (TC11) was examined at 520°C to study the effects of microstructural variation on the dwell sensitivity. Three microstructures (equiaxed, tri-modal and basketweave) were used in this study. When a 3-min dwell time was imposed at the peak of each cycle a significant fatigue life reduction was observed for all microstructures tested. Among the three microstructures, equiaxed microstructure showed the strongest fatigue life reduction. The basketweave microstructure had a little higher dwell-time fatigue life than tri-modal microstructure at low maximum stress levels. In all cases, extensive quasi-cleavage facets and planar slips with track-like dislocations have been intimately linked with the dwell sensitive fatigue response. The amount of quasi-cleavage facets and planar slips decreased with a decrease of the α phase content. A rationalization for planar slip was proposed based on the mechanism of dislocations shearing α₂ particles. It is believed that α₂ particle formation and oxidization effects played an important role in dislocation planar slip.