Tailoring the cage and functionality of POSS for scalable low-dielectric and tough cyanate ester hybrid resin

Zongwu Zhang, Yijie Zhou, Yikang Cao, Xutao Ma, Shumeng Wang, Jian Wang, Ziqian Xiang, Fang Chen, Xiaoyan Ma

科研成果: 期刊稿件文章同行评审

4 引用 (Scopus)

摘要

Although polyhedral oligomeric silsesquioxanes (POSSs) are ideal building blocks to reduce the dielectric constant and loss of cyanate ester (CE) resin, as well as enhancing its toughness, attention has been only focused on conventional ones with a cubic T8 cage and a high functionality of eight. Herein, 2(or 4)EGEP-POSS with a DDSQ-type cage and 2/4epoxy-functionality was synthesized. Such a rational design not only endows the two POSSs with larger hollow structures to reduce the polarization of CE, but also confers them lower functionalities favorable for preventing over-crosslinking. Thus, the low-dielectric property and toughness of CE/2(or 4)EGEP-POSS hybrid resins are further optimized. Specifically, the hybrid resin containing 2 wt% 2EGEP-POSS possesses the lowest dielectric constant of 2.49 (10 GHz), the lowest dielectric loss of 0.008 (10 GHz), and a high impact strength of 27.4 MPa (increased by 114.1%). In addition, its excellent glass transition temperature is well maintained at 279.1 °C, and its power transmission coefficient predicated by finite element simulation is up to 94.2% as a radome working at 10 GHz, which is significantly higher than that of pure CE (85.7%). Overall, this work highlights a promising structure-tailored approach using POSSs for the fabrication of high performance hybrid resin materials for application in wave-transparent fields.

源语言英语
页(从-至)11484-11496
页数13
期刊Journal of Materials Chemistry C
12
30
DOI
出版状态已出版 - 22 6月 2024

指纹

探究 'Tailoring the cage and functionality of POSS for scalable low-dielectric and tough cyanate ester hybrid resin' 的科研主题。它们共同构成独一无二的指纹。

引用此