Synthesis of Si-C-N aligned nanofibers with preeminent electromagnetic wave absorption in ultra-broad band

Zhaochen Li, Fang Ye, Laifei Cheng, Peng Wang, Chuchu Guo, Minghang Li, Litong Zhang

科研成果: 期刊稿件文章同行评审

10 引用 (Scopus)

摘要

As other one-dimensional materials, SiC-based nanofibers possess high temperature resistance and good electromagnetic wave absorption with the absorbing mechanism of polarization loss. To overcome the narrow effective absorbing broadband (EAB) and insufficient reflection coefficient (RC), a kind of Si-C-N aligned nanofiber rich in conducting networks and heterogeneous interfaces was designed to assemble the conductive loss and polarization loss in a proportion of 6 : 4. Synthesized via electrospinning combined with polymer-derived-ceramic methods, the prepared nanofibers showed good degree of orientation, a small diameter less than 300 nm and a multiphase structure containing SiC crystallites, Si3N4 crystallites, a carbon phase and an amorphous Si-O-C-N phase. The crystallization, chemical composition and absorbing performance of nanofibers heat-treated at 1300-1600 °C were investigated in detail. The Si-C-N aligned nanofibers with a small thickness of 2.3 mm prepared at 1300 °C represented prominent absorption that the minimum RC sank down to -54.24 dB at 17.84 GHz, while 3.0 mm-thick nanofibers heated at 1500 °C exhibited ultra-broad EAB that went up to 8.93 GHz (cover 9.07-18 GHz). With the thickness varying from 2.5 mm to 10 mm, EAB gradually shifted from high frequency to low frequency in the measured band of 2-18 GHz. The synergistic effect of conductive loss, polarization loss and good impedance matching contributed to the performed ultrawide EAB and strong absorption. The prepared Si-C-N nanofibers are considered promising candidates of high-temperature-stable absorbents under harsh conditions.

源语言英语
页(从-至)16966-16977
页数12
期刊Journal of Materials Chemistry C
9
47
DOI
出版状态已出版 - 21 12月 2021

指纹

探究 'Synthesis of Si-C-N aligned nanofibers with preeminent electromagnetic wave absorption in ultra-broad band' 的科研主题。它们共同构成独一无二的指纹。

引用此