TY - GEN
T1 - Synthesis and characterization of water based acrylic pressure sensitive adhesive of surface protection tape
AU - He, Min
AU - Zhang, Qiuyu
AU - Guo, Jiying
PY - 2011
Y1 - 2011
N2 - The water based acrylic pressure sensitive adhesive was synthesized by seeded pre-emulsion polymerization, the influence of the amount of seeded pre-emulsion, and tri-functional aziridine crosslinker on the properties of the adhesive were studied. It was found that with the increase of the amount of seeded pre-emulsion, latex particle size decreases, contrasted with the increase of the viscosity, surface tension and contact angle of the emulsion; The aging performance of the adhesive can be significantly improved with the increase of the content of the crosslinker; compared with high temperature, high humidity has a more worse negative effect on the aging performance of the adhesive.
AB - The water based acrylic pressure sensitive adhesive was synthesized by seeded pre-emulsion polymerization, the influence of the amount of seeded pre-emulsion, and tri-functional aziridine crosslinker on the properties of the adhesive were studied. It was found that with the increase of the amount of seeded pre-emulsion, latex particle size decreases, contrasted with the increase of the viscosity, surface tension and contact angle of the emulsion; The aging performance of the adhesive can be significantly improved with the increase of the content of the crosslinker; compared with high temperature, high humidity has a more worse negative effect on the aging performance of the adhesive.
KW - Aging performance
KW - Crosslink
KW - Pressure sensitive adhesive
KW - Surface protection tape
KW - Water based
UR - http://www.scopus.com/inward/record.url?scp=80053091633&partnerID=8YFLogxK
U2 - 10.4028/www.scientific.net/AMR.306-307.1785
DO - 10.4028/www.scientific.net/AMR.306-307.1785
M3 - 会议稿件
AN - SCOPUS:80053091633
SN - 9783037852040
T3 - Advanced Materials Research
SP - 1785
EP - 1791
BT - Emerging Focus on Advanced Materials
T2 - 1st International Congress on Advanced Materials 2011, AM2011
Y2 - 13 May 2011 through 16 May 2011
ER -