Structure, properties and growth mechanism of a self-assembled nanocylindrical MoS 2 /Mo-S-C composite film

Zewen Duan, Li Qiao, Liqiang Chai, Jiao Xu, Peng Wang, Weimin Liu

科研成果: 期刊稿件文章同行评审

34 引用 (Scopus)

摘要

A self-assembled nanocylindrical MoS 2 /M-S-C composite film with excellent tribological properties was synthesized by simultaneously sputtering of MoS 2 and graphite targets. The HRTEM observation of the polished surface and cross-sections reveals that this nanocylindrical structure with MoS 2 -rich phase encircled by carbon matrix arranging alternately in vertical patterns is initiated from the film-substrate interface and continues to the film surface. The XRD results show that this film exhibits dominant (1 0 0) basal planes. In comparison with pure MoS 2 film, this nanocylindrical MoS 2 /Mo-S-C composite film exhibits largely enhanced hardness and higher elastic recovery ratio (d elastic /d max ) under the same load. Surprisingly, the pin-on-disk tribotests in vacuum on it display a low friction-coefficient and long wear lives (up to 5 × 10 5 revolutions). The HRTEM observation of wear tracks finds that the MoS 2 texture was reassembled on the film surface, and a tribofilm with preferential (0 0 2) basal planes in thickness about 100 nm is quickly formed in sliding. Based on the XRD results and TEM images of this film, this clear nanocylindrical structure was attributed to atomic transport occurring preferentially along the edge sites of MoS 2 crystallites.

源语言英语
页(从-至)564-574
页数11
期刊Applied Surface Science
465
DOI
出版状态已出版 - 28 1月 2019
已对外发布

指纹

探究 'Structure, properties and growth mechanism of a self-assembled nanocylindrical MoS 2 /Mo-S-C composite film' 的科研主题。它们共同构成独一无二的指纹。

引用此