Specific heat, thermal diffusivity, and thermal conductivity of Ag–Si alloys within a wide temperature range of 293–823 K

H. M. Chen, Q. Wang, D. L. Geng, H. P. Wang

科研成果: 期刊稿件文章同行评审

10 引用 (Scopus)

摘要

The laser flash method was employed to explore the heat transfer behaviors of Ag-x at.% Si (where x = 0, 5, 11, 25, 50, 75 and 100) alloys over a wide temperature range from 293 to 823 K. The temperature dependency of specific heat and thermal diffusivity were determined by a differential scanning calorimeter and laser flash equipment. Accordingly, the thermal conductivity of Ag–Si alloys was derived. It is found that the thermal conductivity decreases with increasing temperature. At a certain temperature, there is a sharp decline of thermal conductivity with the rising Si content before it reaches the eutectic composition. The decreasing rate of conductivity with rising Si content reduces when Si content is larger than 11%. The microstructures of Ag–Si alloys reveal that the abnormal thermal conductivity at eutectic composition may be caused by the large amount of phase boundaries.

源语言英语
文章编号109997
期刊Journal of Physics and Chemistry of Solids
153
DOI
出版状态已出版 - 6月 2021

指纹

探究 'Specific heat, thermal diffusivity, and thermal conductivity of Ag–Si alloys within a wide temperature range of 293–823 K' 的科研主题。它们共同构成独一无二的指纹。

引用此