Solute segregation behavior of nickel-based single crystal superalloys directionally solidified under transverse static magnetic field

Yong Zhao, Long Hou, Xi Li, Haijun Su, Jun Zhang

科研成果: 期刊稿件文章同行评审

8 引用 (Scopus)

摘要

The solute segregation behavior of Ni-based single crystal (SX) superalloys directionally solidified over wide ranges of solidification rates under various intensities of transverse static magnetic field (TSMF, 0–0.7 T) is systematically investigated. The results show that the influence of TSMF on solute segregation depends on magnetic field intensity and solidification rate. At low solidification rate, the applied TSMF during directional solidification can dramatically suppress the solute segregation, which may lead to a narrow range of segregation and lessen γ/γ' eutectic. The partition coefficients of Ti and W with severe segregation tendency all tend to be near one. The measured results of alloy elements concentration in the mushy zone indicate that the thermoelectric magnetic convection (TEMC) induced by TSMF may obviously change the solute distribution in the melt. On the contrary, at high solidification rate, the applied TSMF has little influence on solute segregation, which may be mainly attributed to the low intensity and reduced action time of the magnetic field. The research results may provide a better understanding on interaction between solidification processing and static magnetic field, which is helpful to develop a new method for segregation control on SX superalloys.

源语言英语
文章编号112914
期刊Materials Characterization
200
DOI
出版状态已出版 - 6月 2023

指纹

探究 'Solute segregation behavior of nickel-based single crystal superalloys directionally solidified under transverse static magnetic field' 的科研主题。它们共同构成独一无二的指纹。

引用此