Research on interdiffusion behavior of Ti-Zr binary alloy in the β phase

Liang Feng; Jinshan Li; Yuwen Cui; Lei Huang; Hongchao Kou; Lian Zhou

Research on interdiffusion behavior of Ti-Zr binary alloy in the β phase

Liang Feng, Jinshan Li, Yuwen Cui, Lei Huang, Hongchao Kou, Lian Zhou

材料学院

科研成果: 期刊稿件 › 文章 › 同行评审

5 引用（Scopus）

摘要

The interdiffusion behavior of Ti-Zr binary alloy in the β phase (950 to 1150°C) was studied through the diffusion couples by EPMA. The interdiffusion coefficients of the Ti-Zr binary alloy were calculated by the Den Broeder method and modified by the Hall method in the concentration limits between 10^-14 and 10^-12 m²/s. The diffusion activation energy Q and frequency factor D₀ were calculated. The results show that Q and D₀ increase at first and then decrease with the increase of Zr concentration and a summit can be got at about 50at% Zr concentration. The impurity diffusion coefficients in concentration limits were calculated by Vignes-Birchenall method and they were compared with the interdiffusion coefficients determined by Hall modification method. It is found that their results are similar.

源语言	英语
页（从-至）	610-614
页数	5
期刊	Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering
卷	40
期	4
出版状态	已出版 - 4月 2011

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{53a535cf6baf40d1a929b9e76fa0c69b,

title = "Research on interdiffusion behavior of Ti-Zr binary alloy in the β phase",

abstract = "The interdiffusion behavior of Ti-Zr binary alloy in the β phase (950 to 1150°C) was studied through the diffusion couples by EPMA. The interdiffusion coefficients of the Ti-Zr binary alloy were calculated by the Den Broeder method and modified by the Hall method in the concentration limits between 10-14 and 10-12 m2/s. The diffusion activation energy Q and frequency factor D0 were calculated. The results show that Q and D0 increase at first and then decrease with the increase of Zr concentration and a summit can be got at about 50at% Zr concentration. The impurity diffusion coefficients in concentration limits were calculated by Vignes-Birchenall method and they were compared with the interdiffusion coefficients determined by Hall modification method. It is found that their results are similar.",

keywords = "Activation energy, Frequency factor, Impurity diffusion coefficients, Interdiffusion coefficients, Ti-Zr binary alloy",

author = "Liang Feng and Jinshan Li and Yuwen Cui and Lei Huang and Hongchao Kou and Lian Zhou",

year = "2011",

month = apr,

language = "英语",

volume = "40",

pages = "610--614",

journal = "Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering",

issn = "1002-185X",

publisher = "Science Press ",

number = "4",

}

TY - JOUR

T1 - Research on interdiffusion behavior of Ti-Zr binary alloy in the β phase

AU - Feng, Liang

AU - Li, Jinshan

AU - Cui, Yuwen

AU - Huang, Lei

AU - Kou, Hongchao

AU - Zhou, Lian

PY - 2011/4

Y1 - 2011/4

N2 - The interdiffusion behavior of Ti-Zr binary alloy in the β phase (950 to 1150°C) was studied through the diffusion couples by EPMA. The interdiffusion coefficients of the Ti-Zr binary alloy were calculated by the Den Broeder method and modified by the Hall method in the concentration limits between 10-14 and 10-12 m2/s. The diffusion activation energy Q and frequency factor D0 were calculated. The results show that Q and D0 increase at first and then decrease with the increase of Zr concentration and a summit can be got at about 50at% Zr concentration. The impurity diffusion coefficients in concentration limits were calculated by Vignes-Birchenall method and they were compared with the interdiffusion coefficients determined by Hall modification method. It is found that their results are similar.

AB - The interdiffusion behavior of Ti-Zr binary alloy in the β phase (950 to 1150°C) was studied through the diffusion couples by EPMA. The interdiffusion coefficients of the Ti-Zr binary alloy were calculated by the Den Broeder method and modified by the Hall method in the concentration limits between 10-14 and 10-12 m2/s. The diffusion activation energy Q and frequency factor D0 were calculated. The results show that Q and D0 increase at first and then decrease with the increase of Zr concentration and a summit can be got at about 50at% Zr concentration. The impurity diffusion coefficients in concentration limits were calculated by Vignes-Birchenall method and they were compared with the interdiffusion coefficients determined by Hall modification method. It is found that their results are similar.

KW - Activation energy

KW - Frequency factor

KW - Impurity diffusion coefficients

KW - Interdiffusion coefficients

KW - Ti-Zr binary alloy

UR - http://www.scopus.com/inward/record.url?scp=79955947347&partnerID=8YFLogxK

M3 - 文章

AN - SCOPUS:79955947347

SN - 1002-185X

VL - 40

SP - 610

EP - 614

JO - Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering

JF - Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering

IS - 4

ER -

Research on interdiffusion behavior of Ti-Zr binary alloy in the β phase

摘要

其它文件与链接

指纹

引用此