摘要

The relationship between weight change and modulus decrease after thermo-exposure of 2D-C/SiC, was analyzed. The 2D-C/SiC composite is fabricated by chemical vapor infiltration of SiC into preform. The preform consists of a stack of cloth which is woven with T300 PAN carbon fiber in two orthogonal directions. It was observed that the weight change is the most severe at 900° C, followed by that at 1200 °C, and by that at 600 °C after thermo-exposure. It was also observed that after 10 h exposure, the change of modulus at 600° C exceeds that at 1200°C.

源语言	英语
页（从-至）	2354-2356
页数	3
期刊	Carbon
卷	44
期	11
DOI	https://doi.org/10.1016/j.carbon.2006.01.031
出版状态	已出版 - 9月 2006

访问文件

10.1016/j.carbon.2006.01.031

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{a4968661f165473b9b8cb143d4827bb4,

title = "Relationship between weight change and modulus decrease after thermo-exposure of 2D-C/SiC",

abstract = "The relationship between weight change and modulus decrease after thermo-exposure of 2D-C/SiC, was analyzed. The 2D-C/SiC composite is fabricated by chemical vapor infiltration of SiC into preform. The preform consists of a stack of cloth which is woven with T300 PAN carbon fiber in two orthogonal directions. It was observed that the weight change is the most severe at 900° C, followed by that at 1200 °C, and by that at 600 °C after thermo-exposure. It was also observed that after 10 h exposure, the change of modulus at 600° C exceeds that at 1200°C.",

keywords = "Carbon composites, Mechanical properties, Oxidation",

author = "Dong Han and Qiao, {Sheng Ru} and Mei Li and Lu, {Guo Feng} and Jun Zhang",

year = "2006",

month = sep,

doi = "10.1016/j.carbon.2006.01.031",

language = "英语",

volume = "44",

pages = "2354--2356",

journal = "Carbon",

issn = "0008-6223",

publisher = "Elsevier Ltd",

number = "11",

}

TY - JOUR

T1 - Relationship between weight change and modulus decrease after thermo-exposure of 2D-C/SiC

AU - Han, Dong

AU - Qiao, Sheng Ru

AU - Li, Mei

AU - Lu, Guo Feng

AU - Zhang, Jun

PY - 2006/9

Y1 - 2006/9

N2 - The relationship between weight change and modulus decrease after thermo-exposure of 2D-C/SiC, was analyzed. The 2D-C/SiC composite is fabricated by chemical vapor infiltration of SiC into preform. The preform consists of a stack of cloth which is woven with T300 PAN carbon fiber in two orthogonal directions. It was observed that the weight change is the most severe at 900° C, followed by that at 1200 °C, and by that at 600 °C after thermo-exposure. It was also observed that after 10 h exposure, the change of modulus at 600° C exceeds that at 1200°C.

AB - The relationship between weight change and modulus decrease after thermo-exposure of 2D-C/SiC, was analyzed. The 2D-C/SiC composite is fabricated by chemical vapor infiltration of SiC into preform. The preform consists of a stack of cloth which is woven with T300 PAN carbon fiber in two orthogonal directions. It was observed that the weight change is the most severe at 900° C, followed by that at 1200 °C, and by that at 600 °C after thermo-exposure. It was also observed that after 10 h exposure, the change of modulus at 600° C exceeds that at 1200°C.

KW - Carbon composites

KW - Mechanical properties

KW - Oxidation

UR - http://www.scopus.com/inward/record.url?scp=33745449429&partnerID=8YFLogxK

U2 - 10.1016/j.carbon.2006.01.031

DO - 10.1016/j.carbon.2006.01.031

M3 - 文章

AN - SCOPUS:33745449429

SN - 0008-6223

VL - 44

SP - 2354

EP - 2356

JO - Carbon

JF - Carbon

IS - 11

ER -

Relationship between weight change and modulus decrease after thermo-exposure of 2D-C/SiC

摘要

访问文件

其它文件与链接

指纹

引用此