Quantitative analysis on microstructure characteristic of pre-strained β-solidified TiAl alloy during post-heat treatment

Fengming Qiang, Xinyu Wu, Yonghao Yu, Meina Cai, Wen Wang, Lulu Li, Yi Liu, Jun Cai, Hongchao Kou, Kuaishe Wang

科研成果: 期刊稿件文章同行评审

摘要

The β/βo phase in β-solidified TiAl alloys plays a contradictory role in improving processability at high temperatures but deteriorating performance at service temperature due to its ordering transformation. After exerting its positive role during thermomechanical processing, it must be eliminated or reduced to a minimum through post-heat treatment. In this study, the microstructural evolution of the pre-strained Ti-43.24Al-8.42Nb-0.20W-0.21B-0.24Y alloy on post-heat treatment is investigated, and a quantitative relationship between βo phase content and the pre-strain is established. Due to the difference in driving force of phase transformation, with decreasing pre-strain the microstructure displays varied characteristics from a mixed structure comprising (α2+γ) lamellar colonies, γ blocks, and βo phase, to a nearly-lamellar structure after post-heat treatment at 1270 °C/4h/FC. Only if the pre-strain is less than 0.78, a refined nearly-lamellar structure can be achieved. This work provides important theoretical guidance for practical forging processing of β-solidified TiAl alloys.

源语言英语
文章编号113662
期刊Vacuum
230
DOI
出版状态已出版 - 12月 2024

指纹

探究 'Quantitative analysis on microstructure characteristic of pre-strained β-solidified TiAl alloy during post-heat treatment' 的科研主题。它们共同构成独一无二的指纹。

引用此