Preparation and oxidation protection of CVD SiC/a-BC/SiC coatings for 3D C/SiC composites

Yongsheng Liu; Litong Zhang; Laifei Cheng; Wenbin Yang; Weihua Zhang; Yongdong Xu

doi:10.1016/j.corsci.2009.01.026

Preparation and oxidation protection of CVD SiC/a-BC/SiC coatings for 3D C/SiC composites

Yongsheng Liu, Litong Zhang, Laifei Cheng, Wenbin Yang, Weihua Zhang, Yongdong Xu

材料学院

Northwestern Polytechnical University Xian

科研成果: 期刊稿件 › 文章 › 同行评审

74 引用（Scopus）

摘要

An amorphous boron carbide (a-BC) coating was prepared by LPCVD process from BCl₃-CH₄-H₂-Ar system. XPS result showed that the boron concentration was 15.0 at.%, and carbon was 82.0 at.%. One third of boron was distributed to a bonding with carbon and 37.0 at.% was dissolved in graphite lattice. A multiple-layered structure of CVD SiC/a-BC/SiC was coated on 3D C/SiC composites. Oxidation tests were conducted at 700, 1000, and 1200 °C in 14 vol.% H₂O/8 vol.% O₂/78 vol.% Ar atmosphere up to 100 h. The 3D C/SiC composites with the modified coating system had a good oxidation resistance. This resulted in the high strength retained ratio of the composites even after the oxidation.

源语言	英语
页（从-至）	820-826
页数	7
期刊	Corrosion Science
卷	51
期	4
DOI	https://doi.org/10.1016/j.corsci.2009.01.026
出版状态	已出版 - 4月 2009

访问文件

10.1016/j.corsci.2009.01.026

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{76c7b339f8954287a1b041b8486abe52,

title = "Preparation and oxidation protection of CVD SiC/a-BC/SiC coatings for 3D C/SiC composites",

abstract = "An amorphous boron carbide (a-BC) coating was prepared by LPCVD process from BCl3-CH4-H2-Ar system. XPS result showed that the boron concentration was 15.0 at.%, and carbon was 82.0 at.%. One third of boron was distributed to a bonding with carbon and 37.0 at.% was dissolved in graphite lattice. A multiple-layered structure of CVD SiC/a-BC/SiC was coated on 3D C/SiC composites. Oxidation tests were conducted at 700, 1000, and 1200 °C in 14 vol.% H2O/8 vol.% O2/78 vol.% Ar atmosphere up to 100 h. The 3D C/SiC composites with the modified coating system had a good oxidation resistance. This resulted in the high strength retained ratio of the composites even after the oxidation.",

keywords = "A. Ceramic matrix composites, B. SEM, B. Weight loss, B. XPS, C. Oxidation",

author = "Yongsheng Liu and Litong Zhang and Laifei Cheng and Wenbin Yang and Weihua Zhang and Yongdong Xu",

year = "2009",

month = apr,

doi = "10.1016/j.corsci.2009.01.026",

language = "英语",

volume = "51",

pages = "820--826",

journal = "Corrosion Science",

issn = "0010-938X",

publisher = "Elsevier Ltd",

number = "4",

}

TY - JOUR

T1 - Preparation and oxidation protection of CVD SiC/a-BC/SiC coatings for 3D C/SiC composites

AU - Liu, Yongsheng

AU - Zhang, Litong

AU - Cheng, Laifei

AU - Yang, Wenbin

AU - Zhang, Weihua

AU - Xu, Yongdong

PY - 2009/4

Y1 - 2009/4

N2 - An amorphous boron carbide (a-BC) coating was prepared by LPCVD process from BCl3-CH4-H2-Ar system. XPS result showed that the boron concentration was 15.0 at.%, and carbon was 82.0 at.%. One third of boron was distributed to a bonding with carbon and 37.0 at.% was dissolved in graphite lattice. A multiple-layered structure of CVD SiC/a-BC/SiC was coated on 3D C/SiC composites. Oxidation tests were conducted at 700, 1000, and 1200 °C in 14 vol.% H2O/8 vol.% O2/78 vol.% Ar atmosphere up to 100 h. The 3D C/SiC composites with the modified coating system had a good oxidation resistance. This resulted in the high strength retained ratio of the composites even after the oxidation.

AB - An amorphous boron carbide (a-BC) coating was prepared by LPCVD process from BCl3-CH4-H2-Ar system. XPS result showed that the boron concentration was 15.0 at.%, and carbon was 82.0 at.%. One third of boron was distributed to a bonding with carbon and 37.0 at.% was dissolved in graphite lattice. A multiple-layered structure of CVD SiC/a-BC/SiC was coated on 3D C/SiC composites. Oxidation tests were conducted at 700, 1000, and 1200 °C in 14 vol.% H2O/8 vol.% O2/78 vol.% Ar atmosphere up to 100 h. The 3D C/SiC composites with the modified coating system had a good oxidation resistance. This resulted in the high strength retained ratio of the composites even after the oxidation.

KW - A. Ceramic matrix composites

KW - B. SEM

KW - B. Weight loss

KW - B. XPS

KW - C. Oxidation

UR - http://www.scopus.com/inward/record.url?scp=62849105031&partnerID=8YFLogxK

U2 - 10.1016/j.corsci.2009.01.026

DO - 10.1016/j.corsci.2009.01.026

M3 - 文章

AN - SCOPUS:62849105031

SN - 0010-938X

VL - 51

SP - 820

EP - 826

JO - Corrosion Science

JF - Corrosion Science

IS - 4

ER -

Preparation and oxidation protection of CVD SiC/a-BC/SiC coatings for 3D C/SiC composites

摘要

访问文件

其它文件与链接

指纹

引用此