Oxidized electroplating zinc-covered carbon fibers as microwave absorption materials

Jun Zeng; Huiqing Fan; Yangli Wang; Shiquan Zhang; Jun Xue; Chenjun Zhang

doi:10.1016/j.jallcom.2012.02.068

Oxidized electroplating zinc-covered carbon fibers as microwave absorption materials

Jun Zeng, Huiqing Fan, Yangli Wang, Shiquan Zhang, Jun Xue, Chenjun Zhang

材料学院

科研成果: 期刊稿件 › 快报 › 同行评审

32 引用（Scopus）

摘要

Zinc oxide nanosheet/zinc-covered carbon fiber composites (ZNSZCFs) were synthesized by annealing the zinc-covered carbon fibers with electroplating in air. The diameter of the ZNSZCFs was about 25 μm. The strongest RL of ZNSZCFs was -32.98 dB at 3.31 GHz. The strong absorption of ZNSZCFs was less than -4 dB (>65%) over the range of 7.54-18 GHz (1.6 mm in thickness) and 5.96-18 GHz (2.0 mm in thickness), respectively. The ZNSZCFs are believed to be ideal microwave absorbing materials.

源语言	英语
页（从-至）	59-62
页数	4
期刊	Journal of Alloys and Compounds
卷	524
DOI	https://doi.org/10.1016/j.jallcom.2012.02.068
出版状态	已出版 - 25 5月 2012

访问文件

10.1016/j.jallcom.2012.02.068

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{09111652f0944584810fee38a6076384,

title = "Oxidized electroplating zinc-covered carbon fibers as microwave absorption materials",

abstract = "Zinc oxide nanosheet/zinc-covered carbon fiber composites (ZNSZCFs) were synthesized by annealing the zinc-covered carbon fibers with electroplating in air. The diameter of the ZNSZCFs was about 25 μm. The strongest RL of ZNSZCFs was -32.98 dB at 3.31 GHz. The strong absorption of ZNSZCFs was less than -4 dB (>65%) over the range of 7.54-18 GHz (1.6 mm in thickness) and 5.96-18 GHz (2.0 mm in thickness), respectively. The ZNSZCFs are believed to be ideal microwave absorbing materials.",

keywords = "Annealing, Electroplating, Microwave absorption, Nanostructures, Oxides, Scanning electron microscopy (SEM)",

author = "Jun Zeng and Huiqing Fan and Yangli Wang and Shiquan Zhang and Jun Xue and Chenjun Zhang",

year = "2012",

month = may,

day = "25",

doi = "10.1016/j.jallcom.2012.02.068",

language = "英语",

volume = "524",

pages = "59--62",

journal = "Journal of Alloys and Compounds",

issn = "0925-8388",

publisher = "Elsevier B.V.",

}

TY - JOUR

T1 - Oxidized electroplating zinc-covered carbon fibers as microwave absorption materials

AU - Zeng, Jun

AU - Fan, Huiqing

AU - Wang, Yangli

AU - Zhang, Shiquan

AU - Xue, Jun

AU - Zhang, Chenjun

PY - 2012/5/25

Y1 - 2012/5/25

N2 - Zinc oxide nanosheet/zinc-covered carbon fiber composites (ZNSZCFs) were synthesized by annealing the zinc-covered carbon fibers with electroplating in air. The diameter of the ZNSZCFs was about 25 μm. The strongest RL of ZNSZCFs was -32.98 dB at 3.31 GHz. The strong absorption of ZNSZCFs was less than -4 dB (>65%) over the range of 7.54-18 GHz (1.6 mm in thickness) and 5.96-18 GHz (2.0 mm in thickness), respectively. The ZNSZCFs are believed to be ideal microwave absorbing materials.

AB - Zinc oxide nanosheet/zinc-covered carbon fiber composites (ZNSZCFs) were synthesized by annealing the zinc-covered carbon fibers with electroplating in air. The diameter of the ZNSZCFs was about 25 μm. The strongest RL of ZNSZCFs was -32.98 dB at 3.31 GHz. The strong absorption of ZNSZCFs was less than -4 dB (>65%) over the range of 7.54-18 GHz (1.6 mm in thickness) and 5.96-18 GHz (2.0 mm in thickness), respectively. The ZNSZCFs are believed to be ideal microwave absorbing materials.

KW - Annealing

KW - Electroplating

KW - Microwave absorption

KW - Nanostructures

KW - Oxides

KW - Scanning electron microscopy (SEM)

UR - http://www.scopus.com/inward/record.url?scp=84862812766&partnerID=8YFLogxK

U2 - 10.1016/j.jallcom.2012.02.068

DO - 10.1016/j.jallcom.2012.02.068

M3 - 快报

AN - SCOPUS:84862812766

SN - 0925-8388

VL - 524

SP - 59

EP - 62

JO - Journal of Alloys and Compounds

JF - Journal of Alloys and Compounds

ER -

Oxidized electroplating zinc-covered carbon fibers as microwave absorption materials

摘要

访问文件

其它文件与链接

指纹

引用此