Oxidation resistant graded multiphase coating for carbon/carbon composites

Xuanru Ren; Hejun Li; Qiangang Fu; Yanhui Chu; Kezhi Li

doi:10.1016/j.surfcoat.2013.06.105

Oxidation resistant graded multiphase coating for carbon/carbon composites

Xuanru Ren, Hejun Li, Qiangang Fu, Yanhui Chu, Kezhi Li

材料学院

Northwestern Polytechnical University Xian

科研成果: 期刊稿件 › 文章 › 同行评审

35 引用（Scopus）

摘要

A double layer TaB₂-TaSi₂-SiC-Si/TaC-SiC coating was prepared on the surface of C/C composites to improve the oxidation resistance of the composites, which was prepared by in situ reaction method through pack cementation technique. The phase composition and microstructures of the multiphase coating were characterized by XRD and SEM-EDS. The inner coating is composed of TaC and SiC, while the outer multiphase coating is composed of TaB₂, TaSi₂, SiC and Si. The multilayer coating is about 200μm in thickness and does not display penetrating crack or big cavities. The coating could protect C/C from oxidation at 1773K in air for 330h with only 0.9% weight loss, thanks to the formed silicate glass layer containing SiO₂ and tantalum oxides.

源语言	英语
页（从-至）	821-826
页数	6
期刊	Surface and Coatings Technology
卷	232
DOI	https://doi.org/10.1016/j.surfcoat.2013.06.105
出版状态	已出版 - 15 10月 2013

访问文件

10.1016/j.surfcoat.2013.06.105

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{8fcc141451c943128de16f9a43fc2b24,

title = "Oxidation resistant graded multiphase coating for carbon/carbon composites",

abstract = "A double layer TaB2-TaSi2-SiC-Si/TaC-SiC coating was prepared on the surface of C/C composites to improve the oxidation resistance of the composites, which was prepared by in situ reaction method through pack cementation technique. The phase composition and microstructures of the multiphase coating were characterized by XRD and SEM-EDS. The inner coating is composed of TaC and SiC, while the outer multiphase coating is composed of TaB2, TaSi2, SiC and Si. The multilayer coating is about 200μm in thickness and does not display penetrating crack or big cavities. The coating could protect C/C from oxidation at 1773K in air for 330h with only 0.9% weight loss, thanks to the formed silicate glass layer containing SiO2 and tantalum oxides.",

keywords = "Carbon/carbon composites, Coating, Oxidation resistance, TaB, TaC",

author = "Xuanru Ren and Hejun Li and Qiangang Fu and Yanhui Chu and Kezhi Li",

year = "2013",

month = oct,

day = "15",

doi = "10.1016/j.surfcoat.2013.06.105",

language = "英语",

volume = "232",

pages = "821--826",

journal = "Surface and Coatings Technology",

issn = "0257-8972",

publisher = "Elsevier B.V.",

}

TY - JOUR

T1 - Oxidation resistant graded multiphase coating for carbon/carbon composites

AU - Ren, Xuanru

AU - Li, Hejun

AU - Fu, Qiangang

AU - Chu, Yanhui

AU - Li, Kezhi

PY - 2013/10/15

Y1 - 2013/10/15

N2 - A double layer TaB2-TaSi2-SiC-Si/TaC-SiC coating was prepared on the surface of C/C composites to improve the oxidation resistance of the composites, which was prepared by in situ reaction method through pack cementation technique. The phase composition and microstructures of the multiphase coating were characterized by XRD and SEM-EDS. The inner coating is composed of TaC and SiC, while the outer multiphase coating is composed of TaB2, TaSi2, SiC and Si. The multilayer coating is about 200μm in thickness and does not display penetrating crack or big cavities. The coating could protect C/C from oxidation at 1773K in air for 330h with only 0.9% weight loss, thanks to the formed silicate glass layer containing SiO2 and tantalum oxides.

AB - A double layer TaB2-TaSi2-SiC-Si/TaC-SiC coating was prepared on the surface of C/C composites to improve the oxidation resistance of the composites, which was prepared by in situ reaction method through pack cementation technique. The phase composition and microstructures of the multiphase coating were characterized by XRD and SEM-EDS. The inner coating is composed of TaC and SiC, while the outer multiphase coating is composed of TaB2, TaSi2, SiC and Si. The multilayer coating is about 200μm in thickness and does not display penetrating crack or big cavities. The coating could protect C/C from oxidation at 1773K in air for 330h with only 0.9% weight loss, thanks to the formed silicate glass layer containing SiO2 and tantalum oxides.

KW - Carbon/carbon composites

KW - Coating

KW - Oxidation resistance

KW - TaB

KW - TaC

UR - http://www.scopus.com/inward/record.url?scp=84883465418&partnerID=8YFLogxK

U2 - 10.1016/j.surfcoat.2013.06.105

DO - 10.1016/j.surfcoat.2013.06.105

M3 - 文章

AN - SCOPUS:84883465418

SN - 0257-8972

VL - 232

SP - 821

EP - 826

JO - Surface and Coatings Technology

JF - Surface and Coatings Technology

ER -

Oxidation resistant graded multiphase coating for carbon/carbon composites

摘要

访问文件

其它文件与链接

指纹

引用此