Oxidation behavior from room temperature to 1500°C of 3D-C/SiC composites with different coatings

科研成果: 期刊稿件文章同行评审

46 引用 (Scopus)

摘要

A carbon-fiber-reinforced silicon carbide composite (3D-C/ SiC) was prepared by chemical vapor infiltration. A SiC and SiC/Si-Zr coating were deposited on the composite to investigate the effect of different coatings on the oxidation behavior of 3D-C/SiC composites. The 3D-C/SiC(SiC/Si-Zr) composite decreased in weight below 1000°C and increased in weight above 1000°C. With an increasing oxidation time, the weight loss increased greatly and the weight gain increased little. The 3D-C/SiC(SiC) composite always decreased in weight over the full temperature range. With an increasing oxidation time, the weight loss increased rapidly below 1000°C and reached its minimum value at 1400°C. The 3D-C/SIC(SiC/Si-Zr) composite had a higher oxidation resistance above 1000°C, and the 3D-C/SiC(SiC) composite had a higher oxidation resistance below 1000°C. The wider the coating cracks, the larger the maximum weight loss and the lower the temperature corresponding to the maximum weight loss. With an increasing oxidation time, the activation energy of the 3D-C/SiC(SiC/Si-Zr) composite increased from 96 to 138 k J/mol, and the 3D-C/SiC(SiC) composite increased from 130 to 180 kJ/mol.

源语言英语
页(从-至)989-991
页数3
期刊Journal of the American Ceramic Society
85
4
DOI
出版状态已出版 - 4月 2002

指纹

探究 'Oxidation behavior from room temperature to 1500°C of 3D-C/SiC composites with different coatings' 的科研主题。它们共同构成独一无二的指纹。

引用此