Nanostructure and surface roughness in the processed surface layer of Ti-6Al-4V via shot peening

Y. G. Liu, M. Q. Li, H. J. Liu

科研成果: 期刊稿件文章同行评审

97 引用 (Scopus)

摘要

Shot peening process of Ti-6Al-4V was performed at the air pressures ranging from 0.15 MPa to 0.35 MPa and processing durations ranging from 15 min to 60 min so as to obtain the effects of the shot peening on the structure characteristic and surface roughness of Ti-6Al-4V. The experimental results showed that the nanocrystalline layer in Ti-6Al-4V could be fabricated via shot peening at the air pressure above 0.25 MPa and the processing duration above 30 min. The thickness of deformation layer and the degree of grain refinement increased with an increase in the air pressure and processing duration, but the corresponding surface became rougher. In order to obtain a good combination between the grain refinement and the surface roughness, shot peening of Ti-6Al-4V should be performed at a smaller air pressure and a longer processing duration.

源语言英语
页(从-至)83-90
页数8
期刊Materials Characterization
123
DOI
出版状态已出版 - 1 1月 2017

指纹

探究 'Nanostructure and surface roughness in the processed surface layer of Ti-6Al-4V via shot peening' 的科研主题。它们共同构成独一无二的指纹。

引用此