Migration of depleted uranium from a corroded penetrator in soil vadose zone in Bosnia and Herzegovina

Depleted uranium (DU) from corroded armor penetrators can migrate through the soil vadose zone and cause environmental problems, yet studies on such migration at former theatres of war are scarce. Here, we investigated vertical DU migration in a soil profile due to a penetrator (3–8 cm beneath the soil surface) corroded over 7 years in Bosnia and Herzegovina. The highest concentration of DU was ∼45,300 mg/kg at 6–10 cm, with the concentration decreasing markedly with increasing depth. The majority of the DU accumulated within the top 20 cm and the DU front reached ∼42 cm beneath the penetrator. In addition, particles with varying U concentrations (3–65 wt%) were observed at 0–15 cm, with U primarily co-located with O, Si, Al, maghemite, and hematite. Particularly, metaschoepite was identified at 6–10 cm. Finally, X-ray absorption spectroscopy analysis found U was hexavalent in the soil profile. These findings suggest that the downward migration of DU was likely present as a soluble form adsorbed on clay minerals and Fe oxides. Overall, we show that the rate of DU migration within the vadose zone is comparatively slow, although if the penetrator is left in the soil for decades, it could pose a serious long-term risk. Environmental Implications: Over 90 % of the depleted uranium (DU) penetrators fired in previous conflicts missed their armored targets and were left in the soil to corrode. The corroded penetrators can not only contaminate soil but also pose a risk to groundwater. The present study examined the migration of DU in a soil profile that included a DU penetrator that had been corroding for over 7 years. Studying the dynamics of DU migration is essential to develop effective remediation strategies to mitigate long-term environmental risks and safeguard ecosystems and human health from DU contamination.